Dynamic recrystallization and texture evolution of Mg-Y-Zn alloy during hot extrusion process | |
Tong, L. B. ; Li, X. ; Zhang, D. P. ; Cheng,L.R. ; Zhang,H.J. | |
刊名 | materials characterization
![]() |
2014 | |
卷号 | 92期号:22页码:77-83 |
关键词 | MECHANICAL-PROPERTIES MICROSTRUCTURE EVOLUTION ELEVATED-TEMPERATURES ORDERED PHASE STRENGTH SHEET TWINS AZ31 |
通讯作者 | zhang,hj |
英文摘要 | the microstructure and texture evolution of mg98.5y1zn0.5 and mg92.5y5zn2.5 (atomic percent) alloys during hot extrusion were systematically investigated. the coarse lpso phases with higher volume fraction (similar to 57%) suppressed the twinning generation in the initial stage of extrusion, and accelerated the dynamic recrystallization through the particle deformation zones. therefore, the volume fraction of drxed grains in as-extruded mg92.5y5zn2.5 alloy was much higher than that of mg98.5y1zn0.5 alloy. the intensive recrystallization process resulted in the conventional basal texture weakening, although the texture evolution was mainly dominated by flow behavior. the dynamic recrystallization behavior in mg92.5y5zn2.5 alloy restricted the formation of deformation texture, and thus the more random texture was observed during the whole extrusion process. (c) 2014 elsevier inc. all rights reserved. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2015-10-27 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/57459] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Tong, L. B.,Li, X.,Zhang, D. P.,et al. Dynamic recrystallization and texture evolution of Mg-Y-Zn alloy during hot extrusion process[J]. materials characterization,2014,92(22):77-83. |
APA | Tong, L. B.,Li, X.,Zhang, D. P.,Cheng,L.R.,&Zhang,H.J..(2014).Dynamic recrystallization and texture evolution of Mg-Y-Zn alloy during hot extrusion process.materials characterization,92(22),77-83. |
MLA | Tong, L. B.,et al."Dynamic recrystallization and texture evolution of Mg-Y-Zn alloy during hot extrusion process".materials characterization 92.22(2014):77-83. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论