GaSe:Er3+ crystals for SHG in the infrared spectral range | |
Feng Z. S. ; Guo J. ; Xie J. J. ; Zhang L. M. ; Gao J. Y. ; Andreev Y. M. ; Izaak T. I. ; Kokh K. A. ; Lanskii G. V. ; Shaiduko A. V. ; Shabalina A. V. ; Svetlichnyi V. A. | |
刊名 | Optics Communications
![]() |
2014 | |
期号 | 318页码:205-211 |
ISSN号 | ISBN/0030-4018 |
英文摘要 | Centimeter-sized Er-doped single crystals were grown from the melts GaSe:Er(0.025, 0.1, 0.5, 1 and 2 at%) by modified vertical Bridgman technology. Real Er content is ascertained as 0.009, 0.019, 0.033, 0.042 and 0.048 at%, respectively. Solubility of Er in GaSe does not exceed 5 x 10(-4). Optimal doping of 0.033 at% of Er was established from SHG experiment. Improved optical quality is identified as a reason of increased nonlinearity for about 24% to that in pure GaSe. New Raman scattering band is found at 2900 cm(-1) that properly related to F-4(9/2)-> I-4(9/2) transition of Er3+ ion. (C) 2013 Elsevier B.V. All rights reserved. |
收录类别 | SCI ; EI |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciomp.ac.cn/handle/181722/44011] ![]() |
专题 | 长春光学精密机械与物理研究所_中科院长春光机所知识产出 |
推荐引用方式 GB/T 7714 | Feng Z. S.,Guo J.,Xie J. J.,et al. GaSe:Er3+ crystals for SHG in the infrared spectral range[J]. Optics Communications,2014(318):205-211. |
APA | Feng Z. S..,Guo J..,Xie J. J..,Zhang L. M..,Gao J. Y..,...&Svetlichnyi V. A..(2014).GaSe:Er3+ crystals for SHG in the infrared spectral range.Optics Communications(318),205-211. |
MLA | Feng Z. S.,et al."GaSe:Er3+ crystals for SHG in the infrared spectral range".Optics Communications .318(2014):205-211. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论