Simple hydrothermal synthesis of mesoporous spinel NiCo2O4 nanoparticles and their catalytic behavior in CH3OH electro-oxidation and H2O2 electro-reduction | |
Ding R ; Qi L ; Jia MJ ; Wang HY | |
刊名 | catalysis science & technology |
2013 | |
卷号 | 3期号:12页码:3207-3215 |
关键词 | PEROXIDE FUEL-CELL WALLED CARBON NANOTUBES LI-ION BATTERIES METHANOL OXIDATION HYDROGEN-PEROXIDE ELECTROCHEMICAL CAPACITORS NICKEL COBALTITE ENERGY-STORAGE LI-O-2 BATTERIES OXYGEN REDUCTION |
ISSN号 | 2044-4753 |
通讯作者 | ding r |
中文摘要 | mesoporous spinel nico2o4 nanoparticles were synthesized via a simple hydrothermal strategy. their physicochemical properties were characterized by x-ray diffraction (xrd), scanning electron microscopy-energy dispersive x-ray spectra (sem-eds), x-ray photoelectron spectra (xps) and nitrogen sorption measurements. their electrocatalytic performances were investigated by cyclic voltammetry (cv), chronoamperomerty (ca) and electrochemical impedance spectroscopy (eis) tests. the obtained nico2o4 materials exhibit a particle size of about 200 nm, a specific surface area (ssa) of 88.94 m(2) g(-1) and a mesopore volume of 0.195 cm(3) g(-1). the binary electroactive sites of co and ni species, high electron conductivity and intriguing mesoporous structures of the nico2o4 electrode favor its desirable electro-catalytic activity. a current density of 93 ma cm(-2) at 0.6 v in 1 m koh and 0.5 m ch3oh electrolytes was obtained for ch3oh electro-oxidation, and a current density of 130 ma cm(-2) at -0.3 v in 3 m naoh and 0.5 m h2o2 electrolytes was achieved for h2o2 electro-reduction. moreover, the nico2o4 electrode exhibits a high stability for both catalytic reactions, showing the potential for further development of high performance non-pt catalysts based alkaline fuel cells (afcs). |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000326988700014 |
公开日期 | 2014-04-16 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/50130] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Ding R,Qi L,Jia MJ,et al. Simple hydrothermal synthesis of mesoporous spinel NiCo2O4 nanoparticles and their catalytic behavior in CH3OH electro-oxidation and H2O2 electro-reduction[J]. catalysis science & technology,2013,3(12):3207-3215. |
APA | Ding R,Qi L,Jia MJ,&Wang HY.(2013).Simple hydrothermal synthesis of mesoporous spinel NiCo2O4 nanoparticles and their catalytic behavior in CH3OH electro-oxidation and H2O2 electro-reduction.catalysis science & technology,3(12),3207-3215. |
MLA | Ding R,et al."Simple hydrothermal synthesis of mesoporous spinel NiCo2O4 nanoparticles and their catalytic behavior in CH3OH electro-oxidation and H2O2 electro-reduction".catalysis science & technology 3.12(2013):3207-3215. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论