Facile synthesis of mesoporous MnO2 microspheres for high performance AC//MnO2 aqueous hybrid supercapacitors | |
Li HH ; Zhang XD ; Ding R ; Qi L ; Wang HY | |
刊名 | electrochimica acta |
2013 | |
卷号 | 108页码:497-505 |
关键词 | ELECTROCHEMICAL CAPACITORS MANGANESE OXIDE ELECTRODE MATERIALS ANODIC DEPOSITION STORAGE PSEUDOCAPACITANCE ULTRACAPACITORS MECHANISM BEHAVIOR DIOXIDES |
ISSN号 | 0013-4686 |
通讯作者 | zhang xd |
中文摘要 | mesoporous manganese oxides (mno2) microspheres were synthesized by the first chemical deposition of manganese carbonate (mnco3) precursors at room temperature and followed by the low-temperature calcinations under 300,350 and 400 degrees c. the obtained mno2 materials exhibit the akhtenskite type mno2 crystalline microstructures and the microspherical morphologies with the diameter of about 1 mu m. the as-synthesized mno2 microspheres under 300 degrees c exhibit the largest specific area (240.5 m(2) g(-1)) and the optimal mesopore volume (0.231 cm(3) g(-1)) than the other two samples under 350 and 400 degrees c (111.4, 106.3 m(2) g(-1); 0.055, 0.021 cm(3) g(-1)), which contribute to the optimal electrochemical performances for supercapacitors. moreover, the as-synthesized mno2 microspheres under 300 degrees c possess the highest tap density (1.156 g cm(-3)) than the other two samples (1.126, 1.043 g cm(-3)), leading to the more feasibility for practical applications in supercapacitors. the as-fabricated mno2 electrode exhibits a high specific capacitance (129 f g(-1) at 0.25 a g(-1)) and high-rate capability (68 f g(-1) at 4a g(-1)). the as-assembled activated carbon (ac)//mno2 hybrid capacitor exhibits a wide working voltage (1.8v), high power and energy densities (2197 w kg(-1) and 12.8w h kg(-1) at 4 a g(-1)), excellent cycling behavior (94.3% capacitance retention after 5000 cycles at 1 a g(-1)), and excellent capacitance recovery performances under different rates (0.25-4 a g(-1)) for tested 4500 cycles, indicating the promising prospective of the easily fabricated mesoporous mno2 microspheres for practical applications in supercapacitors. (c) 2013 elsevier ltd. all rights reserved. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000328014000066 |
公开日期 | 2014-04-15 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/49558] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Li HH,Zhang XD,Ding R,et al. Facile synthesis of mesoporous MnO2 microspheres for high performance AC//MnO2 aqueous hybrid supercapacitors[J]. electrochimica acta,2013,108:497-505. |
APA | Li HH,Zhang XD,Ding R,Qi L,&Wang HY.(2013).Facile synthesis of mesoporous MnO2 microspheres for high performance AC//MnO2 aqueous hybrid supercapacitors.electrochimica acta,108,497-505. |
MLA | Li HH,et al."Facile synthesis of mesoporous MnO2 microspheres for high performance AC//MnO2 aqueous hybrid supercapacitors".electrochimica acta 108(2013):497-505. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论