MAGNETOCRYSTALLINE ANISOTROPY OF OF R(2)FE(10)GA(7) COMPOUNDS WITH R=Y, SM, GD, TB, DY, HO, ER AND TM

CORC > 物理研究所 > 物理所公开发表论文 > 期刊论文

	MAGNETOCRYSTALLINE ANISOTROPY OF OF R(2)FE(10)GA(7) COMPOUNDS WITH R=Y, SM, GD, TB, DY, HO, ER AND TM
	SHEN, BG ; CHENG, ZH ; LIANG, B ; GONG, HY ; ZHANG, JX ; YAN, QW ; ZHAN, WS
刊名	SOLID STATE COMMUNICATIONS
	1995
卷号	96 期号:11 页码:859
关键词	MAGNETIC-PROPERTIES RARE-EARTH INTERMETALLIC COMPOUNDS
ISSN号	0038-1098
通讯作者	SHEN, BG: CHINESE ACAD SCI,INST PHYS,STATE KEY LAB MAGNETISM,POB 603,BEIJING 100080,PEOPLES R CHINA.
中文摘要	Samples with compositions of R(2)Fe(10)Ga(7) (R=Y, Sm, Gd, Tb, Dy, Ho, Er and Tm) were prepared by are-melting. The prepared samples are single phase with the rhombohedral Th2Zn17-type structure. The substitution of Ga in the R(2)Fe(17) results in the increase in unit cell volume. Curie temperatures of R(2)Fe(10)Ga(7), except for Gd compound, are higher than that of R(2)Fe(17). For R(2)Fe(10)Ga(7) compounds with R=Dy and Ho, the Fe sublattice moment and the R sublattice moment cancel occurs at a certain temperature. The compensation temperature T-comp of Dy2Fe10Ga7 and Ho2Fe10Ga7 compounds are found to be 60 and 101 K, respectively. The R(2)Fe(10)Ga(7) compounds with R=Y, Gd, Tb, Dy, Ho, Tm are found to have a uniaxial magnetocrystalline anisotropy at room-temperature; whereas the situation is the reverse for R(2)Fe(10)Ga(7) (R=Sm and Er) which exhibit an easy plane magnetocrystalline anisotropy.
收录类别	SCI
语种	英语
公开日期	2013-09-18
内容类型	期刊论文
源URL	[http://ir.iphy.ac.cn/handle/311004/41633]
专题	物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式 GB/T 7714	SHEN, BG,CHENG, ZH,LIANG, B,et al. MAGNETOCRYSTALLINE ANISOTROPY OF OF R(2)FE(10)GA(7) COMPOUNDS WITH R=Y, SM, GD, TB, DY, HO, ER AND TM[J]. SOLID STATE COMMUNICATIONS,1995,96(11):859.
APA	SHEN, BG.,CHENG, ZH.,LIANG, B.,GONG, HY.,ZHANG, JX.,...&ZHAN, WS.(1995).MAGNETOCRYSTALLINE ANISOTROPY OF OF R(2)FE(10)GA(7) COMPOUNDS WITH R=Y, SM, GD, TB, DY, HO, ER AND TM.SOLID STATE COMMUNICATIONS,96(11),859.
MLA	SHEN, BG,et al."MAGNETOCRYSTALLINE ANISOTROPY OF OF R(2)FE(10)GA(7) COMPOUNDS WITH R=Y, SM, GD, TB, DY, HO, ER AND TM".SOLID STATE COMMUNICATIONS 96.11(1995):859.