Deposition of high-temperature superconducting films on biaxially textured Ni(001) substrates | |
Wang, RP ; Zhou, YL ; Pan, SH ; He, M ; Lu, HB ; Chen, ZH ; Yang, GZ ; Liu, CF ; Wu, X ; Wang, FY ; Feng, Y ; Zhang, PX ; Wu, XZ ; Zhou, L | |
刊名 | PHYSICA C |
2000 | |
卷号 | 337期号:1-4页码:87 |
关键词 | BEAM-ASSISTED DEPOSITION CRITICAL-CURRENT DENSITY O THIN-FILMS LASER DEPOSITION BUFFER LAYERS ALLOYS TAPES |
ISSN号 | 0921-4534 |
通讯作者 | Zhou, YL: Chinese Acad Sci, Ctr Condensed Matter Phys, Beijing 100080, Peoples R China. |
中文摘要 | CeO2//YSZ//YBCO layers have been successfully grown on rolling-assisted biaxially textured Ni(001) substrates using pulsed laser deposition. The results indicate that CeO2 and YSZ can effectively improve film texture. The full-width at half-maximum (FWHM) of the rocking curves for Ni(002), CeO2(002), YSZ(002) and YBCO(005) are 10.8 degrees, 6.8 degrees, 4.7 degrees, 1.2 degrees, respectively. The FWHM of phi-scans for CeO2(202) and YBCO(226) are respectively 9 degrees and 6.5 degrees. Scanning electron microscopy observations reveal that the layer-like morphology was evident from all layers, and Ag can effectively fill in the microcracks and prevent interdiffusion. The critical current density of the best films is 1-2 X 10(6) A/cm(2). (C) 2000 Elsevier Science B.V. All rights reserved. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/35763] |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Wang, RP,Zhou, YL,Pan, SH,et al. Deposition of high-temperature superconducting films on biaxially textured Ni(001) substrates[J]. PHYSICA C,2000,337(1-4):87. |
APA | Wang, RP.,Zhou, YL.,Pan, SH.,He, M.,Lu, HB.,...&Zhou, L.(2000).Deposition of high-temperature superconducting films on biaxially textured Ni(001) substrates.PHYSICA C,337(1-4),87. |
MLA | Wang, RP,et al."Deposition of high-temperature superconducting films on biaxially textured Ni(001) substrates".PHYSICA C 337.1-4(2000):87. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论