Microstructural and Interfacial Characterization of Ti-V Diffusion Bonding Zones | |
Liu GL(刘国亮)3; Ding ML(丁美丽)2; Zhang K(张坤)3; Qu DD(屈丹丹)3; Meng Y(孟洋)3; Luo GX(罗耕星)3; Yang SW1 | |
刊名 | METALS |
2022-12-01 | |
卷号 | 12期号:12页码:15 |
关键词 | Ti-V interface diffusion bonding interface migration martensite transformation recrystallization |
DOI | 10.3390/met12122032 |
通讯作者 | Zhang, Kun(kzhang@imech.ac.cn) ; Qu, Dan-Dan(dandanqu@imech.ac.cn) |
英文摘要 | Ti and V were bonded together and subjected to high-temperature treatment at 1000 or 1100 degrees C for 16 h to study the microstructural evolution and interfacial behavior of Ti-V diffusion interfaces. The samples were prepared by electro-polishing and analyzed using scanning electron microscopy, electron probe microanalysis, electron back-scattered diffraction, and nano-indentation. The results indicated that Ti-V diffusion bonding interfaces comprises a martensite Ti zone, a body-center-cubic Ti (beta-Ti) zone, and a V-based alloy zone. They are divided by two composition interfaces with V contents of similar to 13.5% and similar to 46%. The original interface between the pure Ti and the V alloy substrate falls within the beta-Ti zone. The observation of acicular-martensite rather than lath-martensite is due to the distortion caused by the beta-to-alpha phase transformation in the adjacent pure Ti. The recrystallization of beta-Ti is distributed along the interface direction. The hardness varies across the Ti-V interface bonding zones with the maximum value of 7.9 GPa. |
分类号 | 二类 |
资助项目 | National Natural Science Foundation of China ; [11802309] |
WOS关键词 | TITANIUM-VANADIUM ; STAINLESS-STEEL ; ALLOYS ; PHASE ; TEMPERATURE ; DIFFRACTION ; MARTENSITE |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
WOS记录号 | WOS:000902603100001 |
资助机构 | National Natural Science Foundation of China |
其他责任者 | Zhang, Kun ; Qu, Dan-Dan |
内容类型 | 期刊论文 |
源URL | [http://dspace.imech.ac.cn/handle/311007/91335] |
专题 | 宽域飞行工程科学与应用中心 |
作者单位 | 1.Univ Sci & Technol Beijing, Collaborat Innovat Ctr Steel Technol, Beijing 100083, Peoples R China 2.Peking Univ, Sch & Hosp Stomatol, Clin Div 1, Beijing 100034, Peoples R China; 3.Chinese Acad Sci, Inst Mech, Wide Range Flight Engn Sci & Applicat Ctr, Beijing 100190, Peoples R China; |
推荐引用方式 GB/T 7714 | Liu GL,Ding ML,Zhang K,et al. Microstructural and Interfacial Characterization of Ti-V Diffusion Bonding Zones[J]. METALS,2022,12(12):15. |
APA | 刘国亮.,丁美丽.,张坤.,屈丹丹.,孟洋.,...&Yang SW.(2022).Microstructural and Interfacial Characterization of Ti-V Diffusion Bonding Zones.METALS,12(12),15. |
MLA | 刘国亮,et al."Microstructural and Interfacial Characterization of Ti-V Diffusion Bonding Zones".METALS 12.12(2022):15. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论