Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment

CORC > 兰州化学物理研究所 > 中国科学院兰州化学物理研究所 > 固体润滑国家重点实验室

	Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment
	Zhu Yuhua ; Liu Hao ; Zhang Dongyue ; Wang Jianzhang ; Yan Fengyuan
刊名	Tribology International
	2022
卷号	168 期号:107445 页码:1-9
关键词	Corrosive Wear Sliding Delamination
英文摘要	Monel 400 alloy is widely used in marine engineering due to its corrosion resistance. In this study, the tribo- corrosion behavior of Monel 400 alloy has been investigated under cathodic and anodic polarization conditions. The results revealed that the material loss increased under both cathodic and anodic polarization, while the damage mechanism varied. Under cathodic polarization condition, the damage is caused by delamination of the worn surface and crack propagation in the subsurface, which gets more seriously at more negative polarization values. Under higher anodic polarization values, the lubricating performance of in-situ generated corrosion product was weakened. As the anodic polarization value increased, the diameter of corrosion products increased and got easier to be sheared-off during the sliding process.
语种	英语
内容类型	期刊论文
源URL	[http://ir.licp.cn/handle/362003/29609]
专题	兰州化学物理研究所_固体润滑国家重点实验室
通讯作者	Wang Jianzhang
作者单位	1.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences 2.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences 3.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences 4.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences 5.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences
推荐引用方式 GB/T 7714	Zhu Yuhua,Liu Hao,Zhang Dongyue,et al. Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment[J]. Tribology International,2022,168(107445):1-9.
APA	Zhu Yuhua,Liu Hao,Zhang Dongyue,Wang Jianzhang,&Yan Fengyuan.(2022).Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment.Tribology International,168(107445),1-9.
MLA	Zhu Yuhua,et al."Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment".Tribology International 168.107445(2022):1-9.