Effects of Laves Phase on Burst Behavior of GH3625 Superalloy Pipe During Hot Extrusion | |
Chen Jianjun2; Ding Yutian2; Wang Kun1; Yan Kang2; Ma Yuanjun2; Wang Xingmao2; Zhou Shengming3 | |
刊名 | ACTA METALLURGICA SINICA |
2021 | |
卷号 | 57期号:5页码:641-650 |
关键词 | GH3625 superalloy hot extruded pipe microstructure Laves phase pipe burst |
ISSN号 | 0412-1961 |
DOI | 10.11900/0412.1961.2020.00264 |
英文摘要 | GH3625 superalloy is a type of solid-solution strengthened nickel-based wrought superalloy having Mo and Nb as the main strengthening elements. Because of its excellent high-temperature me-chanical properties and oxidation resistance below 650(o)C, it can be used in harsh stress and atmosphere environments. It is mainly used as a pipe material for aeroengine fuel main pipe, nuclear power steam generator heat transfer pipe, and pressure pipe, etc. Owing to the high alloying degree of nickel-based superalloys, large deformation resistance, and narrow thermal processing temperature range, the pipe preparation process is complicated. In this study, the as-cast and homogenized pipe billets were used for a short-flow hot extrusion pipe preparation test using the same process. The homogenized pipe billet was extruded successfully, and the pipe burst occurred during the extrusion of the as-cast billet. The pipe burst behavior was studied by OM, SEM, and EBSD, with an EDS analysis. The results showed a considerable amount of Laves phases in the as-cast pipe billet, and the Laves phases and micro-segregation were essentially eliminated after homogenization. Adiabatic heating of the as-cast pipe billet leads to the Laves phase remelting during the hot extrusion process, which is the main reason for pipe bursting during a hot extrusion process. The cracking mode of the pipe burst is a quasi-cleavage fracture, combining brittle fracture and ductile fracture with the predominance of the brittle fracture. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 中文 |
出版者 | SCIENCE PRESS |
WOS记录号 | WOS:000642002500008 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/148226] |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.China Natl Nucl Indust Corp, Co Ltd 404, Jiayuguan 735100, Peoples R China; 2.Lanzhou Univ Technol, State Key Lab Adv & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 3.Jinchuan Grp Co Ltd, State Key Lab Nickel & Cobalt Resources Comprehen, Jinchang 737100, Peoples R China |
推荐引用方式 GB/T 7714 | Chen Jianjun,Ding Yutian,Wang Kun,et al. Effects of Laves Phase on Burst Behavior of GH3625 Superalloy Pipe During Hot Extrusion[J]. ACTA METALLURGICA SINICA,2021,57(5):641-650. |
APA | Chen Jianjun.,Ding Yutian.,Wang Kun.,Yan Kang.,Ma Yuanjun.,...&Zhou Shengming.(2021).Effects of Laves Phase on Burst Behavior of GH3625 Superalloy Pipe During Hot Extrusion.ACTA METALLURGICA SINICA,57(5),641-650. |
MLA | Chen Jianjun,et al."Effects of Laves Phase on Burst Behavior of GH3625 Superalloy Pipe During Hot Extrusion".ACTA METALLURGICA SINICA 57.5(2021):641-650. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论