Degradation in durability of magnesium oxychloride-coated reinforced steel concrete | |
Penghui, Wang2; Hongxia, Qiao3; Qiong, Feng1; Hui, Cao1 | |
刊名 | ACI Materials Journal |
2020-04-01 | |
卷号 | 117期号:2页码:33-41 |
关键词 | Bars (metal) Concrete construction Distribution functions Durability Lakes Magnesium compounds Reinforced concrete Soil cement Steel testing Accelerated tests Clayton copula functions Connection function Corrosion current densities Corrosion parameters Degradation factor Magnesium oxychloride Magnesium oxychloride cement |
ISSN号 | 0889325X |
DOI | 10.14359/51720298 |
英文摘要 | Because of ordinary reinforced concrete's poor durability in saline soil areas and Qinghai Salt Lake, magnesium oxychloride-coated steel-cement concrete was adopted in this area. The process of the degradation of coated steel bars' durability was evaluated according to the actual service situation of magnesium-oxychloride-coated reinforced concrete in saline soil areas and Qinghai Salt Lake. The corrosion parameters of coated steel bars in magnesium oxychloride cement concrete were obtained by the accelerated immersion and natural corrosion tests in a drying environment. Using the Copula function as the connection function, the corrosion current density of the coated steel obtained by accelerated tests and natural rust tests was adopted as the degradation factor of the edge distribution function. The results demonstrated that the Clayton-Copula function reflects the actual process of the degradation in durability of coated steel bars well, and the coated steel bars reached a severe state of corrosion at 18,250 days. © 2020 American Concrete Institute. All rights reserved. |
WOS研究方向 | Construction & Building Technology ; Materials Science |
语种 | 英语 |
出版者 | American Concrete Institute |
WOS记录号 | WOS:000571057600004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/150793] |
专题 | 土木工程学院 |
作者单位 | 1.Civil Engineering Laboratory, Lanzhou University of Technology, China 2.Lanzhou University of Technology, Lanzhou, China; 3.Ninety-three Society of Lanzhou University of Technology, China; |
推荐引用方式 GB/T 7714 | Penghui, Wang,Hongxia, Qiao,Qiong, Feng,et al. Degradation in durability of magnesium oxychloride-coated reinforced steel concrete[J]. ACI Materials Journal,2020,117(2):33-41. |
APA | Penghui, Wang,Hongxia, Qiao,Qiong, Feng,&Hui, Cao.(2020).Degradation in durability of magnesium oxychloride-coated reinforced steel concrete.ACI Materials Journal,117(2),33-41. |
MLA | Penghui, Wang,et al."Degradation in durability of magnesium oxychloride-coated reinforced steel concrete".ACI Materials Journal 117.2(2020):33-41. |