Synthesis and lithium storage properties of nitrogen-containing hard carbon from conjugated microporous polymers | |
Zhang, Qingtang1; Zhang, Ya1; Lian, Fei1; Xu, Zongqiang1; Wang, Xiaomei2 | |
刊名 | Ionics |
2022-06-01 | |
卷号 | 28期号:6页码:2623-2633 |
关键词 | Carbon Conjugated polymers Microporosity Nitrogen Pore structure Potassium hydroxide Capacity rate Conjugated microporous polymers Hard carbon High lithium storages KOH activation Lithium storage capacity Lithium storage properties Nitrogen content Pores structure Rate performance |
ISSN号 | 0947-7047 |
DOI | 10.1007/s11581-022-04556-w |
英文摘要 | Two kinds of hard carbons with controllable nitrogen contents (N1HC and N2HC) were prepared from 2,5-dibromopyridine and 2,5-dibromopyrazine, respectively. The nitrogen contents of N1HC and N2HC are 3.75 wt% and 5.08 wt%, respectively. The pore structure of N2HC was further improved by KOH activation and the activated N2HC is designated as N2HC-K. The specific surface area of N2HC-K is considerable 1328.3 m2 g−1, which is distinctly higher than that of N2HC. The rich nitrogen content and developed pores make N2HC-K afford a high lithium storage capacity, rate performance, and excellent cycling performance. The initial reversible capacity of N2HC-K is 604.8 mAh g−1 at a current density of 0.1 A g−1. The specific capacity of N2HC-K after 500 cycles at 0.6 A g−1 is still as high as 488.2 mAh g−1. © 2022, The Author(s), under exclusive licence to Springer-Verlag GmbH Germany, part of Springer Nature. |
语种 | 英语 |
出版者 | Springer Science and Business Media Deutschland GmbH |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/158457] |
专题 | 石油化工学院 材料科学与工程学院 |
作者单位 | 1.Key Laboratory of Low Carbon Energy and Chemical Industry of Gansu Province, School of Petrochemical Engineering, Lanzhou University of Technology, No. 36 Pengjiaping, Qilihe District, Gansu Province, Lanzhou; 730050, China; 2.School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Zhang, Qingtang,Zhang, Ya,Lian, Fei,et al. Synthesis and lithium storage properties of nitrogen-containing hard carbon from conjugated microporous polymers[J]. Ionics,2022,28(6):2623-2633. |
APA | Zhang, Qingtang,Zhang, Ya,Lian, Fei,Xu, Zongqiang,&Wang, Xiaomei.(2022).Synthesis and lithium storage properties of nitrogen-containing hard carbon from conjugated microporous polymers.Ionics,28(6),2623-2633. |
MLA | Zhang, Qingtang,et al."Synthesis and lithium storage properties of nitrogen-containing hard carbon from conjugated microporous polymers".Ionics 28.6(2022):2623-2633. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论