Secondary Solidification Behavior of A356 Aluminum Alloy Prepared by the Self-Inoculation Method | |
Li, Ming2; Li, Yuandong1,2; Huang, Xiaofeng1,2; Ma, Ying1,2; Guan, Renguo2,3 | |
刊名 | METALS
![]() |
2017-07-01 | |
卷号 | 7期号:7 |
关键词 | A356 aluminum alloy semisolid self-inoculation method secondary solidification behavior eutectic structure |
DOI | 10.3390/met7070233 |
英文摘要 | Semisolid slurry of A356 aluminum alloy was prepared by Self-Inoculation Method, and the secondary solidification behavior during rheo-diecasting forming process was researched. The results indicate that the component with non-dendritic and uniformly distributed microstructures can be produced by Rheo-Diecasting (RDC) process (combining Self-inoculation Method (SIM) with High Pressure Die Casting (HPDC)). The isothermal holding time of the slurry has large effect on primary particles, but has little effect on secondary particles. Growth rate of the primary particles in the isothermal holding process conforms to the dynamic equation of Dt(3) - D-0(3) = Kt. The suitable holding time for rheo-diecasting of A356 aluminum alloy is 3 min. During filling process, the nucleation occurs throughout the entire remaining liquid, and nuclei grow stably into globular particles with the limited grain size of 6.5 mu m firstly, then both alpha(1) and alpha(2) particles appear unstable growth phenomenon due to the existence of constitutional undercooling. The average particle sizes and shape factors of both alpha(1) and alpha(2) are decreasing with the increase of filling distance due to different cooling rate in different positions. The growth rate of the eutectic in RDC is 4 times faster than HPDC, which is mainly due to the limitation of alpha(2) particles in RDC process. The average eutectic spacings are decreasing with the increase of filling distance. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000407365900004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/155428] ![]() |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanzhou Univ Technol, Minist Educ, Key Lab Nonferrous Met Alloys & Proc, Lanzhou 730050, Gansu, Peoples R China; 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China; 3.Northeastern Univ, Minist Educ, Key Lab Electromagnet Proc Mat, Shenyang 110819, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Ming,Li, Yuandong,Huang, Xiaofeng,et al. Secondary Solidification Behavior of A356 Aluminum Alloy Prepared by the Self-Inoculation Method[J]. METALS,2017,7(7). |
APA | Li, Ming,Li, Yuandong,Huang, Xiaofeng,Ma, Ying,&Guan, Renguo.(2017).Secondary Solidification Behavior of A356 Aluminum Alloy Prepared by the Self-Inoculation Method.METALS,7(7). |
MLA | Li, Ming,et al."Secondary Solidification Behavior of A356 Aluminum Alloy Prepared by the Self-Inoculation Method".METALS 7.7(2017). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论