Effects of Zn content on microstructures and mechanical properties of Mg-Zn-RE-Sn-Zr-Ca alloys | |
Chen, T.J.; Zhang, D.H.; Wang, W.; Ma, Y.; Hao, Y. | |
刊名 | Materials Science and Engineering A
![]() |
2014-06-23 | |
卷号 | 607页码:17-27 |
关键词 | Binary alloys Calcium alloys Magnesium alloys Mechanical properties Microstructure Neodymium alloys Textures Tin alloys Zircaloy Growth restriction Intergranular modes Mg-Zn-RE alloy Microstructures and mechanical properties Shrinkage porosity Strengthening phase Ternary phase Transgranular modes |
ISSN号 | 09215093 |
DOI | 10.1016/j.msea.2014.03.111 |
英文摘要 | The effects of Zn content on microstructures and mechanical properties of Mg-Zn-RE alloys have been investigated. The results indicate that RE-rich phases will change from the MgY and Mg12Nd binary phases in turn to Z (Mg12ZnRE), Z+W (Mg3Zn3RE2), W and W+I (Mg3Zn6RE) ternary phases as the Zn content increases from 0% to 4%. The grain size decreases when the Zn content increases from 0% to 2% and then increases, which is attributed to the variation of growth restriction factor resulted from the phase changes. The hardness continuously increases due to the formation of the ternary phases and their amount increase. The UTS and elongation first increase as the Zn content increases within the range of 0-2% and then decrease. The W phase is an ideal strengthening phase because the grain bonding strength of the unique W phase-containing alloy is higher than that of the Z or Z+W phase-containing alloy. Shrinkage porosities are easy to generate and the ternary phases distribute more and more continuously due to their amount increase when the Zn content exceeds 2%. The fracture regime changes from intergranular mode to transgranular mode as the Zn content increases from 0% to 2%, and then turns into transgranular mode again. © 2014 Elsevier B.V. |
WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | Elsevier Ltd |
WOS记录号 | WOS:000337644000004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/150370] ![]() |
专题 | 材料科学与工程学院 |
作者单位 | Key Laboratory of Gansu Advanced Nonferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China |
推荐引用方式 GB/T 7714 | Chen, T.J.,Zhang, D.H.,Wang, W.,et al. Effects of Zn content on microstructures and mechanical properties of Mg-Zn-RE-Sn-Zr-Ca alloys[J]. Materials Science and Engineering A,2014,607:17-27. |
APA | Chen, T.J.,Zhang, D.H.,Wang, W.,Ma, Y.,&Hao, Y..(2014).Effects of Zn content on microstructures and mechanical properties of Mg-Zn-RE-Sn-Zr-Ca alloys.Materials Science and Engineering A,607,17-27. |
MLA | Chen, T.J.,et al."Effects of Zn content on microstructures and mechanical properties of Mg-Zn-RE-Sn-Zr-Ca alloys".Materials Science and Engineering A 607(2014):17-27. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论