Corrosion property of arc welding brazed joint between aluminum and steel | |
Gu, Yu-Fen1; Li, Jie2; Shi, Yu1; Huang, Jian-Kang1; Fan, Ding1 | |
刊名 | Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals |
2016-04-01 | |
卷号 | 26期号:4页码:758-765 |
关键词 | Aluminum alloys Aluminum corrosion Annealing Brazing Corrosive effects Dissimilar metals Filler metals Galvanic corrosion Galvanized metal Galvanizing Gas metal arc welding Gas welding Intermetallics Iron alloys Metal analysis Soldered joints Ternary alloys Welds Zinc Zinc alloys Aluminum filler metals Aluminum steel Annealing treatments Corrosion behavior Electrochemical corrosion tests Immersion corrosion tests Intermetallic phasis Zinc rich |
ISSN号 | 10040609 |
英文摘要 | The dissimilar metals of 1060 aluminum alloy and galvanized steel were joined with lap joint by pulsed double electrode gas metal arc welding-brazing with 4043 aluminum filler metal. The welding joints of aluminum and steel were then annealed at 350. The distribution of alloy elements in the welding joint different zones before and after annealing treatment was analyzed by map scanning, and the corrosion behavior of the welding joints was investigated by immersion corrosion tests and electrochemical corrosion tests, the corrosion behavior of the welding joints different zones and the effects of annealing treatment on corrosion property of welding joint were analyzed. The results show that the homogenization diffusion of Si elements in weld seam occurs after annealing treatment, meanwhile, the thickness of Fe2Al5Zn0.4 of zinc-rich zone increases significantly. In addition, the galvanic corrosion occurs when the samples are immersed in corrosive media, the whole steel of welding joint is corroded drastically and displays a homogeneous corrosion, however, the dissolution of weld seam is slight. The intermetallic phases at the interface reduces the corrosion property of welding joints. Further, the results indicate that zinc-rich zone of weld joints is most prone to corrosion. The corrosion behavior of zinc-rich zone was analyzed by map scanning on the basis of the test results. © 2016, Central South University of Technology. All right reserved. |
语种 | 中文 |
出版者 | Central South University of Technology |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/112988] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.School of Aeronautical Materials Engineering, Xi'an Aeronautical Polytechnic Institute, Xi'an; 710089, China |
推荐引用方式 GB/T 7714 | Gu, Yu-Fen,Li, Jie,Shi, Yu,et al. Corrosion property of arc welding brazed joint between aluminum and steel[J]. Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,2016,26(4):758-765. |
APA | Gu, Yu-Fen,Li, Jie,Shi, Yu,Huang, Jian-Kang,&Fan, Ding.(2016).Corrosion property of arc welding brazed joint between aluminum and steel.Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,26(4),758-765. |
MLA | Gu, Yu-Fen,et al."Corrosion property of arc welding brazed joint between aluminum and steel".Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals 26.4(2016):758-765. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论