Synthesis of Different-Sized La0.7Sr0.3MnO3 Nanoparticles via a Polyacrylamide Gel Route and Their Magnetocaloric Properties | |
Wang, Y. F.1,2; Yang, H.1,2 | |
刊名 | JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM
![]() |
2013-12 | |
卷号 | 26期号:12页码:3463-3467 |
关键词 | La0.7Sr0.3MnO3 Nanoparticles Polyacrylamide gel route Chelating agents Magnetocaloric effect |
ISSN号 | 1557-1939 |
DOI | 10.1007/s10948-013-2190-8 |
英文摘要 | In this work, a polyacrylamide gel route was used to synthesize La0.7Sr0.3MnO3 nanoparticles. It is shown that single-phase La0.7Sr0.3MnO3 nanoparticles with a rhombohedral perovskite structure can be prepared at a calcination temperature of 600 A degrees C when separately using citric acid, tartaric acid, acetic acid, oxalic acid, and EDTA as the chelating agent. The particles prepared using the five chelating agents are nearly spherical in shape with a narrow diameter distribution, and have an average size of 24, 28, 36, 38, and 50 nm, respectively. Magnetic properties of the 24 and 50 nm samples (termed as samples S1 and S5, respectively) were investigated. It is revealed that the samples have a similar ferromagnetic Curie temperature T (C) , and exhibit a typical second-order magnetic phase transition near T (C) . The maximum magnetic entropy change at an applied magnetic field of 15 kOe is obtained to be about 0.71 and 0.74 J kg(-1) K-1 for the 24 and 50 nm samples, respectively. |
资助项目 | National Natural Science Foundation of China[50962009][51262018] ; Hongliu Outstanding Talents Foundation of Lanzhou University of Technology[J201205] |
WOS研究方向 | Physics |
语种 | 英语 |
出版者 | SPRINGER |
WOS记录号 | WOS:000325949200017 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/34567] ![]() |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 材料科学与工程学院 理学院 |
通讯作者 | Yang, H. |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Gansu Adv Nonferrous Met Mat, Lanzhou 730050, Peoples R China 2.Lanzhou Univ Technol, Sch Sci, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Y. F.,Yang, H.. Synthesis of Different-Sized La0.7Sr0.3MnO3 Nanoparticles via a Polyacrylamide Gel Route and Their Magnetocaloric Properties[J]. JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM,2013,26(12):3463-3467. |
APA | Wang, Y. F.,&Yang, H..(2013).Synthesis of Different-Sized La0.7Sr0.3MnO3 Nanoparticles via a Polyacrylamide Gel Route and Their Magnetocaloric Properties.JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM,26(12),3463-3467. |
MLA | Wang, Y. F.,et al."Synthesis of Different-Sized La0.7Sr0.3MnO3 Nanoparticles via a Polyacrylamide Gel Route and Their Magnetocaloric Properties".JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM 26.12(2013):3463-3467. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论