Effects of Dy, Sr and Die Casting on Microstructure, Mechanical and Corrosion Properties of Mg-Dy-Sr-Nd-Zr Alloys | |
Liu, Dexue1,2; Yin, Xunyan1,2; Pang, Xin1,2; Hu, Shiwen1,2; Ding, Yutian1,2 | |
刊名 | JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE |
2017-08 | |
卷号 | 26期号:8页码:3983-3992 |
关键词 | resorbable Mg-Dy-Sr-Nd-Zr alloys die casting microstructure mechanical properties corrosion resistance |
ISSN号 | 1059-9495 |
DOI | 10.1007/s11665-017-2850-0 |
英文摘要 | By adding 2, 6 and 10 wt.% Dy and 0.5, 1.5 and 2 wt.% Sr elements to Mg-2.4Nd-0.5Zr alloys and adopting die-casting process for biomedical Mg-10Dy-0.5Sr-2.4Nd-0.5Zr alloys, the effects of Dy and Sr elements and die-casting process on the microstructure, mechanical properties and corrosion resistance of Mg-Dy-Sr-Nd-Zr alloys were investigated. The new biomedical Mg-10Dy-0.5Sr-2.4Nd-0.5Zr alloys were designed, and the grain size of the as-cast new alloy was refined to similar to 70 mu m and distributed equably. The ultimate tensile strength increased with increasing Dy content and decreasing Sr content. The corrosion rate decreased firstly and then increased with increasing Dy content and decreased with increasing Sr content. By adjusting the content of Sr and Dy, the ultimate tensile strength of as-cast new Mg-10Dy-0.5Sr-2.4Nd-0.5Zr alloys increased to 203 MPa, elongation was 7.4%, and the corrosion rate decreased to 0.48 mm/a. The elongation rate increased to 10.2% after the new biomedical alloys were processed by die casting with an refine-grained microstructure of similar to 18 mu m, meanwhile the ultimate tensile strength decreased to 180 MPa, and the corrosion rate was 1.29 mm/a. |
资助项目 | National Nature Science Foundation of China[51365029][51664041] ; Program for Support Projects of Science and Technology in Gansu Province[1604GKCA038] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | SPRINGER |
WOS记录号 | WOS:000407994400037 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33158] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Liu, Dexue |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Me, Langongping Rd 287, Lanzhou 730050, Gansu, Peoples R China 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Langongping Rd 287, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, Dexue,Yin, Xunyan,Pang, Xin,et al. Effects of Dy, Sr and Die Casting on Microstructure, Mechanical and Corrosion Properties of Mg-Dy-Sr-Nd-Zr Alloys[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,2017,26(8):3983-3992. |
APA | Liu, Dexue,Yin, Xunyan,Pang, Xin,Hu, Shiwen,&Ding, Yutian.(2017).Effects of Dy, Sr and Die Casting on Microstructure, Mechanical and Corrosion Properties of Mg-Dy-Sr-Nd-Zr Alloys.JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE,26(8),3983-3992. |
MLA | Liu, Dexue,et al."Effects of Dy, Sr and Die Casting on Microstructure, Mechanical and Corrosion Properties of Mg-Dy-Sr-Nd-Zr Alloys".JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE 26.8(2017):3983-3992. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论