Effects of Previous Electrochemical and Chemical Corrosions on Surface Layer Softening During Electrochemical Cold Drawing of Q235 Bar | |
Chen, T. J.; Yang, B. Q. | |
刊名 | METALS AND MATERIALS INTERNATIONAL |
2021-12-01 | |
卷号 | 27期号:12页码:5299-5313 |
关键词 | Electrochemical cold drawing Electrochemical corrosion Chemical corrosion Surface layer softening Vacancy Additional dislocation flux |
ISSN号 | 1598-9623 |
DOI | 10.1007/s12540-020-00775-w |
英文摘要 | Influences of previous electrochemical corrosion and chemical corrosion in H(2)SO(4)aqueous solution on surface layer softening during electrochemical cold drawing (ECD) of Q235 steel bar were investigated. Results indicate that these two corrosions all further soften the steel during the subsequent ECD and make the ECD to easier conduct, and the effect from the former corrosion is larger than that from the latter one. Two modes of corrosion can slightly soften or plasticize the bar surface layer due to the increased vacancy clusters, but the contribution of this softening or plasticizing itself to the further softening during ECD is very limited, and the further softening should be mainly attributed to the relaxation of dislocations through absorbing the vacancy clusters and the resulted weakening of work hardening. The current applied during the electrochemical corrosion can promote more vacancy clusters to form in a deeper region beneath the bar surface, and thus the relaxing degree for the dislocations and the influence region are larger than those from the chemical corrosion respectively, resulting in the greater softening. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | KOREAN INST METALS MATERIALS |
WOS记录号 | WOS:000554341900001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/155140] |
专题 | 兰州理工大学 |
作者单位 | Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Chen, T. J.,Yang, B. Q.. Effects of Previous Electrochemical and Chemical Corrosions on Surface Layer Softening During Electrochemical Cold Drawing of Q235 Bar[J]. METALS AND MATERIALS INTERNATIONAL,2021,27(12):5299-5313. |
APA | Chen, T. J.,&Yang, B. Q..(2021).Effects of Previous Electrochemical and Chemical Corrosions on Surface Layer Softening During Electrochemical Cold Drawing of Q235 Bar.METALS AND MATERIALS INTERNATIONAL,27(12),5299-5313. |
MLA | Chen, T. J.,et al."Effects of Previous Electrochemical and Chemical Corrosions on Surface Layer Softening During Electrochemical Cold Drawing of Q235 Bar".METALS AND MATERIALS INTERNATIONAL 27.12(2021):5299-5313. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论