Effects of Load and Displacement Amplitude on Fretting Wear Behavior of DLC Film

doi:10.16078/j.tribology.2020090

CORC > 兰州理工大学 > 兰州理工大学

	Effects of Load and Displacement Amplitude on Fretting Wear Behavior of DLC Film
	Jing, Pengfei; Yu, Shurong; Zhang, Kefei; Ma, Banghao
刊名	Mocaxue Xuebao/Tribology
	2021-03-01
卷号	41 期号:2 页码:213-222
关键词	Adhesives Atom lasers Atomic force microscopy Carbon films Chemical analysis Diamond like carbon films Energy dissipation Friction Morphology Optical emission spectroscopy Scanning electron microscopy Titanium alloys Tribology Wear of materials Displacement amplitudes Field emission scanning electron microscopes Fretting friction and wear behavior Fretting wear behavior Laser confocal microscope Laser Raman spectroscopy Self-lubricating properties Unbalanced magnetron sputtering
ISSN号	1004-0595
DOI	10.16078/j.tribology.2020090
英文摘要	In order to improve the fretting wear resistance of TC4 titanium alloy, diamond-like carbon (DLC) films were deposited on the surface of TC4 titanium alloy by unbalanced magnetron sputtering (UBMS) technique. The fretting friction and wear behaviors of DLC film against GCr15 steel ball were studied using a ball-on-flat contact. Under different normal loads and displacement amplitudes, the slip regime and wear mechanism of DLC film were studied with the running condition fretting map(RCFM). The characterization and fretting friction and wear performance of DLC films were carried out by means of atomic force microscopy, nanoindentation, laser Raman spectroscopy, three-dimensional optical profilometer, laser confocal microscope, field emission scanning electron microscope and SRV-V fretting friction and wear tester. The damage mechanism was revealed through the analysis of fretting maps, dissipated energy, the morphology and chemical composition of wear track. The results showed that the displacement amplitude and normal load had great effect on the fretting mode and damage mechanism. The mixed slip regime (MSR) was dominant at the displacement amplitude of 25 μm. On the other hand, the slip regime was gross slip regime (GSR) at the displacement amplitude of 100 μm. The abrasive wear was the main damage mechanism of DLC film under small displacement amplitude, whereas under larger displacement amplitude the wear mechanism of DLC film was mainly adhesive wear. In short, the good fretting wear performance of DLC film in dry friction lies in its excellent mechanical properties and self-lubricating properties. Copyright ©2021 Tribology. All rights reserved.
语种	中文
出版者	Science Press
内容类型	期刊论文
源URL	[http://ir.lut.edu.cn/handle/2XXMBERH/148446]
专题	兰州理工大学
作者单位	College of Petrochemical Engineering, Lanzhou University of Technology, Lanzhou; 730050, China
推荐引用方式 GB/T 7714	Jing, Pengfei,Yu, Shurong,Zhang, Kefei,et al. Effects of Load and Displacement Amplitude on Fretting Wear Behavior of DLC Film[J]. Mocaxue Xuebao/Tribology,2021,41(2):213-222.
APA	Jing, Pengfei,Yu, Shurong,Zhang, Kefei,&Ma, Banghao.(2021).Effects of Load and Displacement Amplitude on Fretting Wear Behavior of DLC Film.Mocaxue Xuebao/Tribology,41(2),213-222.
MLA	Jing, Pengfei,et al."Effects of Load and Displacement Amplitude on Fretting Wear Behavior of DLC Film".Mocaxue Xuebao/Tribology 41.2(2021):213-222.