La2O3-doped 0.6Y(2)O(3)-0.4YCr(0.5)Mn(0.5)O(3) composite NTC ceramics for wide range of temperature sensing | |
Zhang Bo; Zhao Qing; Chang Aimin; Huang Xia; Hou Juan; Zhao Pengjun; Ji Guang | |
刊名 | JOURNAL OF ALLOYS AND COMPOUNDS |
2013 | |
卷号 | 581期号:12页码:573-578 |
关键词 | Wide temperature range NTC thermistors Perovskites La2O3 |
ISSN号 | 0925-8388 |
通讯作者 | Zhao, Q |
中文摘要 | Ceramic compositions based on 0.6Y(2)O(3)-0.4YCr(0.5)Mn(0.5)O(3) doped with La2O3 were prepared by solid state reaction at different calcining temperatures, and sintered at 1550 and 1600 degrees C. XRD patterns have shown that there exists a LaCr0.5Mn0.5O3 phase when the amount of La2O3 increases to 5.0 wt% in the calcined powders. Major phases presented in the sintered ceramics are Y2O3 phase and orthorhombic perovskite phase isomorphic to YCrO3. The obtained q25, B25/150 and B700/1000 constants of the La2O3-doped NTC thermistors are in the range of 105-106 X cm, 3600-3800 K and 6000-6600 K, respectively. The electrical conductivity in these compounds may be due to the presence of Cr3+, Cr4+, Mn3+ and Mn4+ on octahedral sites. The resistance almost does not change when the aging time is from 600 to 1000 h. Such ceramics could be used as potential candidates for NTC thermistors in a wide temperature range from ambient to 1100 degrees C. |
学科主题 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
收录类别 | SCI |
资助信息 | National Natural Science Foundation of China 51102276; Natural Science Foundation of Xinjiang of China 2010211A59; High Technology Research and Development Program of Xinjiang of China 201116147; National High Technology Research and Development Program of China 2012 AA091102 |
公开日期 | 2013-11-07 |
内容类型 | 期刊论文 |
源URL | [http://ir.xjipc.cas.cn/handle/365002/2627] |
专题 | 新疆理化技术研究所_新疆维吾尔自治区电子信息材料与器件重点实验室 |
作者单位 | Chinese Acad Sci, Xinjiang Tech Inst Phys & Chem, Key Lab Funct Mat & Devices Special Environm, Xinjiang Key Lab Elect Informat Mat & Devices, Urumqi 830011, Peoples R China; Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang Bo,Zhao Qing,Chang Aimin,et al. La2O3-doped 0.6Y(2)O(3)-0.4YCr(0.5)Mn(0.5)O(3) composite NTC ceramics for wide range of temperature sensing[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2013,581(12):573-578. |
APA | Zhang Bo.,Zhao Qing.,Chang Aimin.,Huang Xia.,Hou Juan.,...&Ji Guang.(2013).La2O3-doped 0.6Y(2)O(3)-0.4YCr(0.5)Mn(0.5)O(3) composite NTC ceramics for wide range of temperature sensing.JOURNAL OF ALLOYS AND COMPOUNDS,581(12),573-578. |
MLA | Zhang Bo,et al."La2O3-doped 0.6Y(2)O(3)-0.4YCr(0.5)Mn(0.5)O(3) composite NTC ceramics for wide range of temperature sensing".JOURNAL OF ALLOYS AND COMPOUNDS 581.12(2013):573-578. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论