Synthesis of H4Mn5O12 Nanotubes Lithium Ion Sieve and Its Adsorption Properties for Li+ from Aqueous Solution

doi:10.1002/slct.201901764

CORC > 青海盐湖研究所 > 中国科学院青海盐湖研究所 > 盐湖资源与化学实验室

	Synthesis of H4Mn5O12 Nanotubes Lithium Ion Sieve and Its Adsorption Properties for Li+ from Aqueous Solution
	Xu, Naicai; Li, Sixia; Guo, Min; Qian, Zhiqiang; Li, Wu; Liu, Zhong
刊名	CHEMISTRYSELECT
	2019-09-06
卷号	4 期号:33 页码:9562-9569
ISSN号	2365-6549
DOI	10.1002/slct.201901764
英文摘要	Li4Mn5O12 with nanotubes morphology was successfully prepared by hydrothermal and solid phase reaction. The asobtained adsorbent was determined by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM) and N2 ad/desorption technologies. The characterization results indicated that spinel H4Mn5O12 took on two-dimensional nanotubes morphology with the diameter of pore similar to 200 nm, BET surface area is 92.997 m(2).g(-1), and the corresponding pore size centers at 3.4, 35.9 and 156.5 nm. The adsorption experimental results showed that the maximum Li+ adsorption capacity of H4Mn5O12 was as high as 37.0 mg.g(-1), and the adsorption process fit well with Langmuir model. In addition, adsorption kinetic experimental data were well fitted by the pseudo-second-order model, which indicated the adsorption process followed chemisorption involving in ion exchange. The effects of co-existing cations on lithium recovery suggested that Na+, K+, Ca2+ and Mg2+ ions had very small effect on recovery of lithium. The regeneration of H4Mn5O12 for the multicyclic Li+ adsorption and desorption were also assessed. The result implied that most of Li+ could be desorbed within 40 min, but the adsorption capacity decreased when the number of cycles was five, which indicated that the structure of H4Mn5O12 was needed to be improved. Lithium adsorption onto H4Mn5O12 could be attributed to electrostatic interaction and ion exchange between Li+ and H+ according to the results of adsorption isotherm and kinetics properties.
内容类型	期刊论文
源URL	[http://ir.isl.ac.cn/handle/363002/34109]
专题	青海盐湖研究所_盐湖资源与化学实验室中国科学院青海盐湖研究所
推荐引用方式 GB/T 7714	Xu, Naicai,Li, Sixia,Guo, Min,et al. Synthesis of H4Mn5O12 Nanotubes Lithium Ion Sieve and Its Adsorption Properties for Li+ from Aqueous Solution[J]. CHEMISTRYSELECT,2019,4(33):9562-9569.
APA	Xu, Naicai,Li, Sixia,Guo, Min,Qian, Zhiqiang,Li, Wu,&Liu, Zhong.(2019).Synthesis of H4Mn5O12 Nanotubes Lithium Ion Sieve and Its Adsorption Properties for Li+ from Aqueous Solution.CHEMISTRYSELECT,4(33),9562-9569.
MLA	Xu, Naicai,et al."Synthesis of H4Mn5O12 Nanotubes Lithium Ion Sieve and Its Adsorption Properties for Li+ from Aqueous Solution".CHEMISTRYSELECT 4.33(2019):9562-9569.