Effect of interaction between H and He on micro-defects in Fe9Cr alloy investigated by slow positron beam | |
Li, Lei1,2; Jin, Shuoxue2; Zhang, Peng2; Wang, Dandan1; Cao, Xingzhong2; Guo, Liping3; Xu, Qiu4; Li, Jun5; Zhang, Tongmin5; Li, Liben1 | |
刊名 | JOURNAL OF NUCLEAR MATERIALS |
2019-12-01 | |
卷号 | 526页码:5 |
关键词 | H/He Sequential irradiation Micro-defects Fe9Cr alloy |
ISSN号 | 0022-3115 |
DOI | 10.1016/j.jnucmat.2019.151748 |
通讯作者 | Jin, Shuoxue(jinshuoxue@ihep.ac.cn) ; Wang, Dandan(wangdan106021@126.com) |
英文摘要 | In order to investigate the effect of interaction between H and He ions on micro-defects in Fe9Cr alloy, well-annealed Fe9Cr alloy were pre-damaged firstly with 1 MeV Ni ions to a dose of 3.4 x 10(13)/cm(2), and then irradiated with single (H or He) ion beam and sequential (H/He or He/H) ions beam. The irradiation were performed with 50 keV H ions, 80 keV He ions with doses of 1 x 10(16)/cm(2) and 2 x 10(15)/cm(2) at 723 K, respectively. Results of slow positron beam show that the S parameter decreased obviously after single (H or He) ions beam irradiation compared to the pre-damaged specimen, which indicate H or He (H-n or Hen) clusters deposit at the damage area caused by Ni ion irradiation and they occupy vacancy sites (V-m), resulting in the formation of numerous HnVm or HenVm clusters. The S parameter induced by He/H ions sequential irradiation didn't change significantly compared to that by single He ion irradiation. However, obvious increment of the S parameter induced by H/He ion sequential irradiation is higher than that induced by singe H ion irradiation. The binding energy of HnVmHe is larger than HenVmH, and it is difficult for subsequent H ions irradiation to decompose the HenVm complexes. (C) 2019 Elsevier B.V. All rights reserved. |
资助项目 | National Natural Science Foundation of China[11505192] ; National Natural Science Foundation of China[U1732265] ; National Natural Science Foundation of China[11705046] ; National Natural Science Foundation of China[11775162] ; National Natural Science Foundation of China[11775236] ; Science and Technology on Surface Physics and Chemistry Laboratory[020204417] |
WOS关键词 | VACANCY-COMPLEXES ; IRRADIATION ; HYDROGEN ; HELIUM ; FE ; EVOLUTION ; IRON ; BEHAVIOR ; STEEL ; IONS |
WOS研究方向 | Materials Science ; Nuclear Science & Technology |
语种 | 英语 |
出版者 | ELSEVIER |
WOS记录号 | WOS:000500777900007 |
资助机构 | National Natural Science Foundation of China ; Science and Technology on Surface Physics and Chemistry Laboratory |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.186/handle/113462/141244] |
专题 | 中国科学院近代物理研究所 |
通讯作者 | Jin, Shuoxue; Wang, Dandan |
作者单位 | 1.Henan Univ Sci & Technol, Sch Phys & Engn, Luoyang 471023, Peoples R China 2.Chinese Acad Sci, Inst High Energy Phys, Multidisciplinary Res Div, Beijing 100049, Peoples R China 3.Wuhan Univ, Sch Phys & Technol, Key Lab Artificial Micro & Nanostruct, Minist Educ, Wuhan 430072, Hubei, Peoples R China 4.Kyoto Univ, Inst Integrated Radiat & Nucl Sci, Kumatori, Osaka 5900494, Japan 5.Chinese Acad Sci, Inst Modern Phys, Lanzhou 730000, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Lei,Jin, Shuoxue,Zhang, Peng,et al. Effect of interaction between H and He on micro-defects in Fe9Cr alloy investigated by slow positron beam[J]. JOURNAL OF NUCLEAR MATERIALS,2019,526:5. |
APA | Li, Lei.,Jin, Shuoxue.,Zhang, Peng.,Wang, Dandan.,Cao, Xingzhong.,...&Wang, Baoyi.(2019).Effect of interaction between H and He on micro-defects in Fe9Cr alloy investigated by slow positron beam.JOURNAL OF NUCLEAR MATERIALS,526,5. |
MLA | Li, Lei,et al."Effect of interaction between H and He on micro-defects in Fe9Cr alloy investigated by slow positron beam".JOURNAL OF NUCLEAR MATERIALS 526(2019):5. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论