Effect of Concrete Micro-Mechanical Properties under the Coupled Corrosion of Sulfate and High Water Head | |
Li, Ruixin1; Hou, Huiming2; Hu, Dawei3; Zou, Yiquan1 | |
刊名 | ENERGIES |
2021-08-01 | |
卷号 | 14期号:16页码:21 |
关键词 | micro-indentation high water head sulfate attack micromechanics |
DOI | 10.3390/en14165039 |
英文摘要 | Large-scale water infrastructure such as immersed tunnels remain in a seawater environment for a long time, and gradually deteriorate under the action of high water head, soil pressure and corrosive ions in seawater solution. In order to simulate the corrosion damage and deterioration of concrete in seawater environment, 10% Na2SO4 solution was used to conduct indoor corrosion tests on concrete samples under different water heads and for different durations. The corrosion damage and micro-mechanical properties of concrete under the coupled action of high water head and sulfate are studied by micro-indentation tests. The effect of sulfate ion corrosion and complex mechanical loading was studied. The effect of micro-mechanical properties of concrete is studied on time and space. Numerical simulation and test results show that the results of micro-indentation are in good agreement with the fitting curves. The chemical damage rate and the corrosion depth increase with the increase of water head; the numerical simulation analysis shows that the sulfate concentration is high in the area where the mechanical damage variable is large, which indicates that the two kinds of corrosion occur in concrete and interact with each other. |
资助项目 | Chinese national key research and development project[2018YFC0809601] ; Jiangxi Province Natural Science Foundation[20202BABL214052] ; Hubei Province Technological Innovation Special Large Project[2017AAA128] ; National Natural Science Foundation of China[51779252] |
WOS研究方向 | Energy & Fuels |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000689273800001 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.198/handle/2S6PX9GI/27853] |
专题 | 中科院武汉岩土力学所 |
通讯作者 | Zou, Yiquan |
作者单位 | 1.Hubei Univ Technol, Sch Civil Architecture & Environm, Wuhan 430068, Peoples R China 2.Shantou Univ, Coll Engn, Shantou 515063, Peoples R China 3.Chinese Acad Sci, Inst Rock & Soil Mech, Wuhan 430071, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Ruixin,Hou, Huiming,Hu, Dawei,et al. Effect of Concrete Micro-Mechanical Properties under the Coupled Corrosion of Sulfate and High Water Head[J]. ENERGIES,2021,14(16):21. |
APA | Li, Ruixin,Hou, Huiming,Hu, Dawei,&Zou, Yiquan.(2021).Effect of Concrete Micro-Mechanical Properties under the Coupled Corrosion of Sulfate and High Water Head.ENERGIES,14(16),21. |
MLA | Li, Ruixin,et al."Effect of Concrete Micro-Mechanical Properties under the Coupled Corrosion of Sulfate and High Water Head".ENERGIES 14.16(2021):21. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论