Fabrication of high strength carbon nanotube/7055Al composite by powder metallurgy combined with subsequent hot extrusion | |
Ma, Kai1,2; Liu, ZhenYu1; Zhang, XingXing1; Xiao, BoLu1; Ma, ZongYi1 | |
刊名 | SCIENCE CHINA-TECHNOLOGICAL SCIENCES |
2021-03-23 | |
页码 | 11 |
关键词 | carbon nanotube aluminum matrix composite hot extrusion bimodal mechanical property |
ISSN号 | 1674-7321 |
DOI | 10.1007/s11431-020-1715-8 |
通讯作者 | Liu, ZhenYu(zyliu@imr.ac.cn) |
英文摘要 | Bimodal carbon nanotube reinforced 7055Al (CNT/7055Al) composites containing coarse grain bands and ultra-fine grain zones were fabricated by high energy ball milling, vacuum hot pressing followed by hot extrusion. The effect of extrusion temperature varied from 320 degrees C to 420 degrees C on the microstructure evolution and tensile properties were investigated. Microstructure observation indicates that the elongated coarse grain bands aligned along the extrusion direction after extrusion. The width of the coarse grain bands increased, and the length of the coarse grain bands increased firstly and then decreased with the increase of extrusion temperature. The grain size of the ultra-fine grain zones changed little after hot extrusion, but the ultra-fine grains coarsened after subsequent heat treatment, especially for the composite extruded at low temperature of 320 degrees C. By observing the CNT distribution, it was found that the higher temperature extrusion was beneficial to the CNT orientation along the extrusion direction. Furthermore, a precipitate free zone formed at the boundary between the coarse grain band and the ultra-fine grain zone as the composite extruded at high temperature of 420 degrees C. As the result of the comprehensive influence of the above microstructure, the tensile strength of the composite extruded at moderate temperature of 370 degrees C reached the highest of 826 MPa. |
资助项目 | Key Research Program of Frontier Sciences, CAS[QYZDJ-SSW-JSC015] ; Project of Manned Spaceflight[040103] ; National Natural Science Foundation of China[51931009] ; National Natural Science Foundation of China[51871214] ; National Natural Science Foundation of China[51871215] ; Youth Innovation Promotion Association CAS[2020197] |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | SCIENCE PRESS |
WOS记录号 | WOS:000632777900001 |
资助机构 | Key Research Program of Frontier Sciences, CAS ; Project of Manned Spaceflight ; National Natural Science Foundation of China ; Youth Innovation Promotion Association CAS |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/162016] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Liu, ZhenYu |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shi Changxu Innovat Ctr Adv Mat, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Ma, Kai,Liu, ZhenYu,Zhang, XingXing,et al. Fabrication of high strength carbon nanotube/7055Al composite by powder metallurgy combined with subsequent hot extrusion[J]. SCIENCE CHINA-TECHNOLOGICAL SCIENCES,2021:11. |
APA | Ma, Kai,Liu, ZhenYu,Zhang, XingXing,Xiao, BoLu,&Ma, ZongYi.(2021).Fabrication of high strength carbon nanotube/7055Al composite by powder metallurgy combined with subsequent hot extrusion.SCIENCE CHINA-TECHNOLOGICAL SCIENCES,11. |
MLA | Ma, Kai,et al."Fabrication of high strength carbon nanotube/7055Al composite by powder metallurgy combined with subsequent hot extrusion".SCIENCE CHINA-TECHNOLOGICAL SCIENCES (2021):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论