Oxidation and cracking behaviors of triple-layered Cr2AlC coating | |
Li, Jingjing1; Xiang, Huimin2; Xu, Jingjun3; Zheng, Lili4; Qian, Yuhai5 | |
刊名 | SURFACE & COATINGS TECHNOLOGY
![]() |
2021-09-25 | |
卷号 | 422页码:8 |
关键词 | Cr2AlC coating Oxidation Diffusion barrier Cracking Internal stress evolution |
ISSN号 | 0257-8972 |
DOI | 10.1016/j.surfcoat.2021.127554 |
通讯作者 | Li, Jingjing(jjli@alum.imr.ac.cn) |
英文摘要 | Cr2AlC coating has potential applications as high temperature protective coating. However, inevitable inter-diffusion at coating/substrate interface promotes Al depletion and deteriorates its oxidation resistance. In the present work, the oxidation behavior of a triple-layered Cr2AlC coating, with (Cr,Al)(2)O-3 inner layer, amorphous intermediate layer and crystalline Cr2AlC outer layer, was investigated at 900 and 1000 degrees C in air. The effect of the (Cr,Al)(2)O(3 )inner layer as diffusion barrier was evaluated during the oxidation process. It is showed that the triple-layered Cr2AlC coating could effectively improve the oxidation resistance of the M38G alloy substrate, due to the Cr2AlC outer layer. The (Cr,Al)(2)O-3 inner layer could prohibit internal nitridation and retard interdiffusion at the coating/substrate interface, improving oxidation resistance of the triple-layered Cr2AlC coating. Furthermore, cracking of the triple-layered Cr2AlC coating was found after oxidation at 900 and 1000 degrees C, due to the thermal stress and internal stress introduced by intermediate amorphous layer crystallization during oxidation. |
资助项目 | National Natural Science Foundation of China[52071318] ; Shenyang Ligong University High Level Talents Research Support Plan[1010147000901] |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000685607200054 |
资助机构 | National Natural Science Foundation of China ; Shenyang Ligong University High Level Talents Research Support Plan |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/159238] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Li, Jingjing |
作者单位 | 1.Shenyang Ligong Univ, Sch Mat Sci & Engn, Shenyang 110159, Peoples R China 2.Aerosp Res Inst Mat & Proc Technol, Beijing 100076, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 4.Qingdao Univ, Coll Mech & Elect Engn, Natl Engn Res Ctr Intelligent Elect Vehicle Power, Qingdao 266071, Peoples R China 5.Aluminum Valley Ind Technol Inst, Zouping 256200, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Jingjing,Xiang, Huimin,Xu, Jingjun,et al. Oxidation and cracking behaviors of triple-layered Cr2AlC coating[J]. SURFACE & COATINGS TECHNOLOGY,2021,422:8. |
APA | Li, Jingjing,Xiang, Huimin,Xu, Jingjun,Zheng, Lili,&Qian, Yuhai.(2021).Oxidation and cracking behaviors of triple-layered Cr2AlC coating.SURFACE & COATINGS TECHNOLOGY,422,8. |
MLA | Li, Jingjing,et al."Oxidation and cracking behaviors of triple-layered Cr2AlC coating".SURFACE & COATINGS TECHNOLOGY 422(2021):8. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论