Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature | |
Yang, Lanlan1; Wang, Jinlong2,3; Yang, Ruize1; Yang, Shasha4; Jia, Yixuan4; Chen, Minghui2,3; Qiao, Yanxin1; Guo, Pingyi1; Zhu, Shenglong2; Wang, Fuhui3,4 | |
刊名 | CORROSION SCIENCE |
2021-03-01 | |
卷号 | 180页码:11 |
关键词 | Superalloys Metal coatings Oxidation |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2020.109182 |
通讯作者 | Wang, Jinlong(wangjinlong@mail.neu.edu.cn) ; Chen, Minghui(mhchen@mail.neu.edu.cn) |
英文摘要 | Oxidation behavior of the nanocrystalline coating with low content of Ta on the N5 single-crystal superalloy is investigated at 1050 and 1150 degrees C. Results indicate that when the content of Ta in the nanocrystalline coating is reduced to 3 wt%, no gamma'-Ni-3(Al, Ta) will not be precipitated during oxidation. Then the activity of Ta is low, it will not be oxidized, which can be stable in the coating after oxidation. Therefore, the oxidation resistance of the nanocrystalline coating with low content of Ta in significantly improved. |
资助项目 | National Natural Science Foundation of China[51671053] ; National Natural Science Foundation of China[51471177] ; National Natural Science Foundation of China[52001142] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000609497900001 |
资助机构 | National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/159044] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Wang, Jinlong; Chen, Minghui |
作者单位 | 1.Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Jiangsu, Peoples R China 2.Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China 3.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Yang, Lanlan,Wang, Jinlong,Yang, Ruize,et al. Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature[J]. CORROSION SCIENCE,2021,180:11. |
APA | Yang, Lanlan.,Wang, Jinlong.,Yang, Ruize.,Yang, Shasha.,Jia, Yixuan.,...&Wang, Fuhui.(2021).Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature.CORROSION SCIENCE,180,11. |
MLA | Yang, Lanlan,et al."Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature".CORROSION SCIENCE 180(2021):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论