Effect of laser incident energy on microstructures and mechanical properties of 12CrNi2Y alloy steel by direct laser deposition

CORC > 金属研究所 > 中国科学院金属研究所

	Effect of laser incident energy on microstructures and mechanical properties of 12CrNi2Y alloy steel by direct laser deposition
	Guan Tingting 1; Chen Suiyuan 1; Chen Xueting 1; Liang Jing 1; Liu Changsheng 1; Wang Mei 2
刊名	JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
	2019
卷号	35 期号:2 页码:395-402
关键词	PROCESSING PARAMETERS UNDERCOOLED AUSTENITE DEFORMATION COMPONENTS MORPHOLOGY STRESS Direct laser deposition Energy area density 12CrNi2Y alloy steel Microstructures Mechanical properties
ISSN号	1005-0302
英文摘要	This work aims to establish the effect of laser energy area density (EAD) as the laser incident energy on density, microstructures and mechanical properties of direct laser deposition (DLD) 12CrNi2Y alloy steel. The results show that the density of DLD 12CrNi2Y alloy steel increases at initial stage and then decreases with an increase of EAD, the highest density of alloy steel sample is 98.95%. The microstructures of DLD 12CrNi2Y alloy steel samples are composed of bainite, ferrite and carbide. With increase of EAD, the microstructures transform from polygonal ferrite (PF) to granular bainite (GB). The martensite-austenite constituent (M-A) in GB transforms from flake-like paralleling to the bainite ferrite laths to granular morphology. It is also found that the average width of laths in finer GB can be refined from 532 nm to 302 nm, which improves the comprehensive properties of DLD 12CrNi2Y alloy steel such as high hardness of 342 +/- 9 HV0.2, yield strength of 702 +/- 16 MPa, tensile strength of 901 +/- 14 MPa and large elongation of 15.2%+/- 0.6%. The DLD 12CrNi2Y material with good strength and toughness could meet the demand of alloy steel components manufacturing. (C) 2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
资助项目	[National Key R&D Program of China] ; [Green Manufacturing System Integration Project of the Industry and Information Ministry of China (2017)] ; [Research and development plan for the future emerging industries in Shenyang]
语种	英语
CSCD记录号	CSCD:6445290
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/157738]
专题	金属研究所_中国科学院金属研究所
作者单位	1.上海市地震局 2.中国科学院金属研究所
推荐引用方式 GB/T 7714	Guan Tingting,Chen Suiyuan,Chen Xueting,et al. Effect of laser incident energy on microstructures and mechanical properties of 12CrNi2Y alloy steel by direct laser deposition[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(2):395-402.
APA	Guan Tingting,Chen Suiyuan,Chen Xueting,Liang Jing,Liu Changsheng,&Wang Mei.(2019).Effect of laser incident energy on microstructures and mechanical properties of 12CrNi2Y alloy steel by direct laser deposition.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(2),395-402.
MLA	Guan Tingting,et al."Effect of laser incident energy on microstructures and mechanical properties of 12CrNi2Y alloy steel by direct laser deposition".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.2(2019):395-402.