Fracture mechanism of transient liquid phase bonding joint of gamma '-strengthened Co-based single crystal superalloy | |
Wang, S. Y.; Sun, Y.; Hou, X. Y.; Cui, C. Y.; Sun, X. F.; Zhou, Y. Z. | |
刊名 | MATERIALS LETTERS |
2020 | |
卷号 | 258 |
DOI | 10.1016/j.matlet.2019.126730 |
英文摘要 | Herein, gamma'-strengthened Co-based single crystal superalloy is bonded by a transient liquid phase bonding process and the fracture process of TLP joint is investigated by using in-situ tensile characterization. The results reveal that boride-induced cracks emerged in the diffusion affected zone, which prefer to stay near the base metal and gradually move towards the isothermally solidified zone. The failure of TLP joint occurs due to the coalescence of cracks, rendering a relatively flat fracture path in the diffusion affected zone. (C) 2019 Published by Elsevier B.V. |
WOS记录号 | WOS:000500934600028 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/155727] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Wang, S. Y.,Sun, Y.,Hou, X. Y.,et al. Fracture mechanism of transient liquid phase bonding joint of gamma '-strengthened Co-based single crystal superalloy[J]. MATERIALS LETTERS,2020,258. |
APA | Wang, S. Y.,Sun, Y.,Hou, X. Y.,Cui, C. Y.,Sun, X. F.,&Zhou, Y. Z..(2020).Fracture mechanism of transient liquid phase bonding joint of gamma '-strengthened Co-based single crystal superalloy.MATERIALS LETTERS,258. |
MLA | Wang, S. Y.,et al."Fracture mechanism of transient liquid phase bonding joint of gamma '-strengthened Co-based single crystal superalloy".MATERIALS LETTERS 258(2020). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论