Oxidation and cracking resistances of La2O3 modified ZrB2-SiC coating on SiC coated graphite in static air | |
Ren, Yan1,2; Qian, Yuhai2; Xu, Jingjun2; Zuo, Jun2; Li, Meishuan2 | |
刊名 | MATERIALS CHEMISTRY AND PHYSICS |
2020-09-01 | |
卷号 | 251页码:9 |
关键词 | Ultra-high temperature ceramic coating Oxidation resistance Graphite Siliconizing |
ISSN号 | 0254-0584 |
DOI | 10.1016/j.matchemphys.2020.123157 |
通讯作者 | Qian, Yuhai(yhqian@imr.ac.cn) |
英文摘要 | A La2O3 modified ZrB2-SiC coating on SiC coated graphite was prepared by slurry brushing and subsequent siliconizing. The coating exhibited much better oxidation and cracking resistances compared with ZrB2-SiC coating. The weight gain of ZrB2-SiC-La2O3 coated sample was 3.85 x 10(-3) g/cm(2) after isothermal oxidation at 1800 degrees C for 30 min and it was 6.49 x 10(-3) g/cm(2) after short cyclic oxidation at 1500 degrees C for 30 times, while they were 4.25 x 10(-3) g/cm(2) and -7.12 x 10(-3) g/cm(2) for the ZrB2-SiC coated sample, respectively. The good comprehensive performance of La2O3 modified ZrB2-SiC coating was attributed to the continuous La dissolved oxide scale with lower oxygen permeability and lower internal stress. |
资助项目 | National Natural Science Foundation of China[51571203] ; National Natural Science Foundation of China[51571205] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000549319900055 |
资助机构 | National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/139817] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Qian, Yuhai |
作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Ren, Yan,Qian, Yuhai,Xu, Jingjun,et al. Oxidation and cracking resistances of La2O3 modified ZrB2-SiC coating on SiC coated graphite in static air[J]. MATERIALS CHEMISTRY AND PHYSICS,2020,251:9. |
APA | Ren, Yan,Qian, Yuhai,Xu, Jingjun,Zuo, Jun,&Li, Meishuan.(2020).Oxidation and cracking resistances of La2O3 modified ZrB2-SiC coating on SiC coated graphite in static air.MATERIALS CHEMISTRY AND PHYSICS,251,9. |
MLA | Ren, Yan,et al."Oxidation and cracking resistances of La2O3 modified ZrB2-SiC coating on SiC coated graphite in static air".MATERIALS CHEMISTRY AND PHYSICS 251(2020):9. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论