The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress | |
Shen, Qiuyan1,2; Yuan, Zhanwei1,2; Liu, Huan1,2; Zhang, Xuemin2; Fu, Qinqin4; Wang, Quanzhao3 | |
刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING |
2020-04-24 | |
卷号 | 782页码:11 |
关键词 | SiCp/Al composite Damage behavior Fracture mechanism Finite element method Stress-state |
ISSN号 | 0921-5093 |
DOI | 10.1016/j.msea.2020.139274 |
通讯作者 | Yuan, Zhanwei(yuanyekingfly@163.com) ; Wang, Quanzhao(qzhwang@imr.ac.cn) |
英文摘要 | In this paper, the deformation, fracture and damage behavior of SiCp/Al composites are studied by experiments and finite element analysis. The crack cracking process of the material was observed by in-situ tensile test, it was found that the composite first produced microcracks near the particles, and the cracks mainly spread to depth and then to both sides. It is determined by a tensile test that the fracture mechanism of the material is the tearing of the aluminum matrix and the peeling between the particles and the matrix. The tensile damage mechanism of the composite material in three directions (rolling direction, rolling transverse direction and rolling normal direction) and different strains were determined. It is found that in the process of tensile deformation, microcracks are first formed at the defects (voids) and weak interfaces, and many fine cracks converge together to form large cracks leading to the fracture of the material, during which a few particles fall off, but there is no particle fracture. The global and local tensile tests of the composites were simulated by finite element method, the results of the stress-strain state under different strains and the effects of particles on the materials are analyzed in detail, and the validity of the test results is determined. |
资助项目 | China Postdoctoral Science Foundation[2017M623084] ; National Science and Technology Major Project[2017-VII-0012-0107] ; Fundamental Research Funds for the Central Universities, CHD[310831172001] ; Fundamental Research Funds for the Central Universities, CHD[300102319101] ; Fundamental Research Funds for the Central Universities, CHD[300102310201] |
WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000525797900023 |
资助机构 | China Postdoctoral Science Foundation ; National Science and Technology Major Project ; Fundamental Research Funds for the Central Universities, CHD |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/138232] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Yuan, Zhanwei; Wang, Quanzhao |
作者单位 | 1.Changan Univ, Lab Adv Technol & Equipment, Xian 710061, Shaanxi, Peoples R China 2.Changan Univ, Sch Mat Sci & Engn, Xian 710061, Shaanxi, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 4.Xi An Jiao Tong Univ, Ctr Advancing Mat Performance Nanoscale CAMP Nano, HARCC, State Key Lab Mech Behav Mat, Xian 710049, Shaanxi, Peoples R China |
推荐引用方式 GB/T 7714 | Shen, Qiuyan,Yuan, Zhanwei,Liu, Huan,et al. The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2020,782:11. |
APA | Shen, Qiuyan,Yuan, Zhanwei,Liu, Huan,Zhang, Xuemin,Fu, Qinqin,&Wang, Quanzhao.(2020).The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,782,11. |
MLA | Shen, Qiuyan,et al."The damage mechanism of 17vol.%SiCp/Al composite under uniaxial tensile stress".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 782(2020):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论