Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium | |
Zhang, Xu1,2,3; Li, Dianzhong1; Li, Yiyi1; Lu, Shanping1 | |
刊名 | CORROSION SCIENCE |
2019-10-01 | |
卷号 | 159页码:13 |
关键词 | Austenitic weld metal SEM XRD High temperature corrosion Oxidation |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2019.108137 |
通讯作者 | Lu, Shanping(shplu@imr.ac.cn) |
英文摘要 | The isothermal oxidation behaviors of the Fe-25Cr-20Ni-chi Nb (0-1.6 wt.%) weld metals have been investigated in air at 1100 degrees C. Results showed that niobium has a detrimental effect on the elevated temperature oxidation resistance of the chromia-forming weld metals. In the Nb content range studied, the Nb content of 1.6 wt.% showed the most deleterious effect on the chromia layer. Niobium promoted the chromium depletion underneath the oxide/matrix interface by impeding the chromium diffusion, which ruined the compactness of the chromia layer. The oxidation of niobium at the oxide layer/metal interface can further cause severe damage to the chromia layer, resulting in catastrophic oxide spallation. |
资助项目 | Key Research Program of Chinese Academy of Sciences[ZDRW-CN-2017-1] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000488143500027 |
资助机构 | Key Research Program of Chinese Academy of Sciences |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/135626] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Lu, Shanping |
作者单位 | 1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110014, Liaoning, Peoples R China 3.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Xu,Li, Dianzhong,Li, Yiyi,et al. Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium[J]. CORROSION SCIENCE,2019,159:13. |
APA | Zhang, Xu,Li, Dianzhong,Li, Yiyi,&Lu, Shanping.(2019).Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium.CORROSION SCIENCE,159,13. |
MLA | Zhang, Xu,et al."Oxidation behaviors of Fe-25Cr-20Ni-chi Nb austenitic weld metals at 1100 degrees C in ambient air: Role of elemental niobium".CORROSION SCIENCE 159(2019):13. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论