The influence of defect and temperature on the fatigue behaviours of Al-Si-Cu-Mg-Ni alloy | |
Liu, Haiquan1,2; Pang, Jianchao2; Wang, Meng1,2; Li, Jianping3; Guo, Yongchun3; Li, Shouxin2; Zhang, Zhefeng1,2 | |
刊名 | FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES |
2019-07-15 | |
页码 | 11 |
关键词 | Al-Si-Cu-Mg-Ni alloys casting defects fatigue damage high temperature high-cycle fatigue |
ISSN号 | 8756-758X |
DOI | 10.1111/ffe.13099 |
通讯作者 | Pang, Jianchao(jcpang@imr.ac.cn) ; Zhang, Zhefeng(zhfzhang@imr.ac.cn) |
英文摘要 | High-cycle fatigue (HCF) properties of two Al-Si-Cu-Mg-Ni alloys with different defect sizes named as alloys A (smaller ones) and B (bigger ones) were investigated at 350 degrees C and 425 degrees C, respectively. The results indicate that fatigue strengths of both alloys decrease as the temperature increases. Fatigue cracks originated from pores and oxide films at both temperatures. They propagated preferentially through cracked matrix at 350 degrees C and debonded interface and grain boundary at 425 degrees C. Alloy A exhibits higher fatigue life and fatigue strength than alloy B at 350 degrees C due to its smaller pore sizes. However, it has slightly worse fatigue properties than alloy B at 425 degrees C because the fatigue crack initiation is controlled by oxide film at this temperature and is not affected by its size. This indicates that there is a transition of predominant initiation site from pores to oxide films when the temperature increases. The fatigue strength estimated through defect size is consistent with the experimental results at 350 degrees C, while unsuitable at 425 degrees C. |
资助项目 | National Natural Science Foundation of China (NSFC)[51331007] ; National Natural Science Foundation of China (NSFC)[51871224] |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | WILEY |
WOS记录号 | WOS:000476321400001 |
资助机构 | National Natural Science Foundation of China (NSFC) |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/134798] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Pang, Jianchao; Zhang, Zhefeng |
作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Mat Fatigue & Fracture Lab, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 3.Xian Technol Univ, Sch Mat & Chem Engn, Xian 710021, Shaanxi, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, Haiquan,Pang, Jianchao,Wang, Meng,et al. The influence of defect and temperature on the fatigue behaviours of Al-Si-Cu-Mg-Ni alloy[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES,2019:11. |
APA | Liu, Haiquan.,Pang, Jianchao.,Wang, Meng.,Li, Jianping.,Guo, Yongchun.,...&Zhang, Zhefeng.(2019).The influence of defect and temperature on the fatigue behaviours of Al-Si-Cu-Mg-Ni alloy.FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES,11. |
MLA | Liu, Haiquan,et al."The influence of defect and temperature on the fatigue behaviours of Al-Si-Cu-Mg-Ni alloy".FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES (2019):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论