Effect of interfacial reaction behaviour on the clogging of SEN in the continuous casting of bearing steel containing rare earth elements

doi:10.1016/j.jallcom.2019.04.010

CORC > 金属研究所 > 中国科学院金属研究所

	Effect of interfacial reaction behaviour on the clogging of SEN in the continuous casting of bearing steel containing rare earth elements
	Tian, Chen 1; Yu, Jingkun 1; Jin, Endong 1; Wen, Tianpeng 1; Jia, Danbin 1; Liu, Zhenli 1; Fu, Paixian 2; Yuan, Lei 1
刊名	JOURNAL OF ALLOYS AND COMPOUNDS
	2019-07-05
卷号	792 页码:1-7
关键词	Rare earth steel Submerged entry nozzle Decarburization layer Clogging
ISSN号	0925-8388
DOI	10.1016/j.jallcom.2019.04.010
通讯作者	Yuan, Lei(yuanl@smm.neu.edu.cn)
英文摘要	The problem of the clogging of submerged entry nozzle (SEN) in the continuous casting of bearing steel containing rare earth (RE) elements is studied in this paper. The composition, formation process, growth mode and cause of the clogging at the interface of the molten steel and the refractory of SEN were analysed in detail during the process of molten steel casting. The results showed that the graphite dissolution process on the inner wall of SEN can improve the wettability between the molten steel and the refractories, which provides convenient conditions for the reaction and adhesion of RE and its compounds on the inner wall of the SEN. Clogging compounds at different locations had different compositions. The main compositions at the interface between the molten steel and the refractories were consisting of cerium aluminate compounds, while the outer walls of the SEN mostly consisted of cerium sulfide compounds. With the growth of clogging, the laminar flow interface layer on the inner wall of the SEN will gradually increase, which further accelerates the clogging, and ultimately affects the continuous casting. Therefore, the prevention of clogging in the SEN of RE steel can be mainly carried out by inhibiting the formation of initial clogging in the early stages and by inhibiting the reaction of the SEN materials. (c) 2019 Published by Elsevier B.V.
资助项目	National Natural Science Foundation of China[51874083] ; National Natural Science Foundation of China[51404056] ; Fundamental Research Funds for the Central Universities[N182504009]
WOS研究方向	Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	ELSEVIER SCIENCE SA
WOS记录号	WOS:000467235800001
资助机构	National Natural Science Foundation of China ; Fundamental Research Funds for the Central Universities
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/133188]
专题	金属研究所_中国科学院金属研究所
通讯作者	Yuan, Lei
作者单位	1.Northeastern Univ, Sch Met, Shenyang 110819, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式 GB/T 7714	Tian, Chen,Yu, Jingkun,Jin, Endong,et al. Effect of interfacial reaction behaviour on the clogging of SEN in the continuous casting of bearing steel containing rare earth elements[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2019,792:1-7.
APA	Tian, Chen.,Yu, Jingkun.,Jin, Endong.,Wen, Tianpeng.,Jia, Danbin.,...&Yuan, Lei.(2019).Effect of interfacial reaction behaviour on the clogging of SEN in the continuous casting of bearing steel containing rare earth elements.JOURNAL OF ALLOYS AND COMPOUNDS,792,1-7.
MLA	Tian, Chen,et al."Effect of interfacial reaction behaviour on the clogging of SEN in the continuous casting of bearing steel containing rare earth elements".JOURNAL OF ALLOYS AND COMPOUNDS 792(2019):1-7.