Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl | |
Li, Wen-Bo1; Liu, Lan-Lan1; Yang, Ying-Fei2; Zhu, Sheng-Long3; Wang, Fu-Hui3 | |
刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS |
2019-05-01 | |
卷号 | 32期号:5页码:599-606 |
关键词 | Corrosion Composite coating Ti-47Al-2Cr-2Nb alloy Diffusion |
ISSN号 | 1006-7191 |
DOI | 10.1007/s40195-018-0842-1 |
通讯作者 | Yang, Ying-Fei(yfyang@jnu.edu.cn) |
英文摘要 | Type I hot corrosion behavior of SiO2-Al2O3-glass composite coating based on Ti-47Al-2Cr-2Nb substrate was investigated in the mixture salt of 25wt%NaCl+75wt%Na2SO4 at 850 degrees C. The results showed that there was a bidirectional ion exchange between composite coating and the film of mixed salts, and the sodium ion in the molten salts penetrated into the glass matrix of composite coating, while the potassium ion in the glass matrix dissolved into the molten salts. A decrease in hot corrosion rate was achieved for the coated alloy in comparison with the bared substrate due to the composite coating acting as a diffusion barrier to sulfur and chlorine and preventing the molten salts from diffusing to the coating/alloy interface during the hot corrosion exposure. Additionally, the composite coating decreased the oxygen partial pressure at the coating/alloy interface and promoted the selective oxidation of Al to form a protective Al2O3 layer. |
资助项目 | National Natural Science Foundation of China[51201171] ; National High Technology Research and Development Program of China (863 Program)[2012AA03A512] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
WOS记录号 | WOS:000463780700007 |
资助机构 | National Natural Science Foundation of China ; National High Technology Research and Development Program of China (863 Program) |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/132944] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Yang, Ying-Fei |
作者单位 | 1.Hunan Elect Power Co Ltd, Changsha, Hunan, Peoples R China 2.Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, Guangzhou 510632, Guangdong, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Lab Corros & Protect, Shenyang 110016, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Wen-Bo,Liu, Lan-Lan,Yang, Ying-Fei,et al. Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2019,32(5):599-606. |
APA | Li, Wen-Bo,Liu, Lan-Lan,Yang, Ying-Fei,Zhu, Sheng-Long,&Wang, Fu-Hui.(2019).Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl.ACTA METALLURGICA SINICA-ENGLISH LETTERS,32(5),599-606. |
MLA | Li, Wen-Bo,et al."Hot Corrosion Behavior of SiO2-Al2O3-Glass Composite Coating on Ti-47Al-2Cr-2Nb Alloy: Diffusion Barrier for S and Cl".ACTA METALLURGICA SINICA-ENGLISH LETTERS 32.5(2019):599-606. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论