Hydrogen-assisted fracture features of a high strength ferrite-pearlite steel | |
Jiang, Yuefeng1,3; Zhang, Bo1; Wang, Dongying2; Zhou, Yu1; Wang, Jianqiu1; Han, En-Hou1; Ke, Wei1 | |
刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY |
2019-06-01 | |
卷号 | 35期号:6页码:1081-1087 |
关键词 | Ferrite-pearlite steel TEM Fracture Hydrogen embrittlement |
ISSN号 | 1005-0302 |
DOI | 10.1016/j.jmst.2018.12.019 |
通讯作者 | Zhang, Bo(bxz011@imr.ac.cn) |
英文摘要 | Up to now, the exact reason of hydrogen-induced fracture for ferrite-pearlite (FP) steel is still not fully understood. This study presents detail observations of the feature beneath the fracture surface with the aim to reveal the hydrogen-induced cracking initiation and propagation processes. Slow strain rate tensile (SSRT) testing shows that the FP steel is sensitive to hydrogen embrittlement (HE). Focused ion beam (FIB) was used to prepare samples for TEM observations after HE fracture. The corresponding fractographic morphologies of hydrogen charged specimen exhibit intergranular (IG) and quasi-cleavage (QC) fracture feature. Pearlite colony, ferrite/pearlite (F/P) boundary and the adjacent ferrite matrix are found to be responsible for the initial HE fracture and the subsequent propagation. With increasing of the stress intensity factor, fracture mode is found to change from mixed IG and QC to entire QC feature which only occurs at the ferrite matrix. No crack is observed at the ferrite/cementite (F/C) interface. This may be mainly due to the limited pearlite lamella size and relatively low interface energy. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
资助项目 | Joint Funds of the National Natural Science Foundation of China[U1608257] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | JOURNAL MATER SCI TECHNOL |
WOS记录号 | WOS:000464017000016 |
资助机构 | Joint Funds of the National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/132847] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhang, Bo |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China 2.Shenyang Blower Works Grp Corp, Shenyang 110869, Liaoning, Peoples R China 3.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Jiang, Yuefeng,Zhang, Bo,Wang, Dongying,et al. Hydrogen-assisted fracture features of a high strength ferrite-pearlite steel[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2019,35(6):1081-1087. |
APA | Jiang, Yuefeng.,Zhang, Bo.,Wang, Dongying.,Zhou, Yu.,Wang, Jianqiu.,...&Ke, Wei.(2019).Hydrogen-assisted fracture features of a high strength ferrite-pearlite steel.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,35(6),1081-1087. |
MLA | Jiang, Yuefeng,et al."Hydrogen-assisted fracture features of a high strength ferrite-pearlite steel".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 35.6(2019):1081-1087. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论