Fabrication of Cr2AlC coating from a cost-efficient Cr-Al-C target by arc ion plating | |
Li, Yueming2,3; Zhao, Guorui1; Du, Beining2; Li, Meishuan3; Xu, Jingjun3; Qian, Yuhai3; Sheng, Liyuan2; Zheng, Yufeng2 | |
刊名 | SURFACE INNOVATIONS |
2019-03-01 | |
卷号 | 7期号:1页码:12-17 |
关键词 | annealing coatings physical vapor deposition |
ISSN号 | 2050-6252 |
DOI | 10.1680/jsuin.18.00037 |
通讯作者 | Qian, Yuhai(yhqian@imr.ac.cn) |
英文摘要 | In the present research, a novel cost-efficient chromium (Cr)-aluminum (Al)-carbon (C) target hot-pressed at 650 degrees C with chromium:aluminum:carbon = 2:1:1 (molar ratio) was applied to fabricate chromium aluminum carbide (Cr2AlC) coatings by the arc ion plating method at room temperature and subsequent annealing. Scanning electron microscopy, X-ray diffraction and transmission electron microscopy were used to characterize the coatings and the target. The results showed that the chromium-aluminum-carbon target mainly comprised chromium, carbon and chromium aluminum compound (Cr9Al17). By arc ion plating with the hot-pressed chromium-aluminum-carbon target and subsequent annealing at 620 degrees C, polycrystalline chromium aluminum carbide coating with minor chromium carbide (Cr3C2) was obtained. The as-prepared chromium aluminum carbide coating was dense and crack-free, and there existed macroparticles in the coating. Transmission electron microscopy observations revealed that the as-prepared chromium aluminum carbide coating exhibited a multilayer structure vertical to the growth direction. The coating possessed hardness and adhesion strength of 8.8 +/- 0.8 GPa and 42 +/- 17 MPa, respectively, which could meet the basic requirement of high-temperature protective coating. |
资助项目 | Shenzhen Technology Innovation Project[JSGG20170412145203293] ; Shenzhen Basic Research Project[JCYJ20170815153143221] ; Shenzhen Basic Research Project[JCYJ20160427170611414] ; National Science Foundation of China[51571205] |
WOS研究方向 | Chemistry ; Materials Science |
语种 | 英语 |
出版者 | ICE PUBLISHING |
WOS记录号 | WOS:000455273300003 |
资助机构 | Shenzhen Technology Innovation Project ; Shenzhen Basic Research Project ; National Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/131415] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Qian, Yuhai |
作者单位 | 1.Guangdong Inst New Mat, Natl Engn Lab Modern Mat Surface Engn Technol, Guangzhou, Guangdong, Peoples R China 2.Peking Univ, Shenzhen Inst, Shenzhen, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Yueming,Zhao, Guorui,Du, Beining,et al. Fabrication of Cr2AlC coating from a cost-efficient Cr-Al-C target by arc ion plating[J]. SURFACE INNOVATIONS,2019,7(1):12-17. |
APA | Li, Yueming.,Zhao, Guorui.,Du, Beining.,Li, Meishuan.,Xu, Jingjun.,...&Zheng, Yufeng.(2019).Fabrication of Cr2AlC coating from a cost-efficient Cr-Al-C target by arc ion plating.SURFACE INNOVATIONS,7(1),12-17. |
MLA | Li, Yueming,et al."Fabrication of Cr2AlC coating from a cost-efficient Cr-Al-C target by arc ion plating".SURFACE INNOVATIONS 7.1(2019):12-17. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论