Influence of Scandium Addition on Stress Corrosion Cracking Susceptibility of Al-Zn-Mg Alloy in Different Corrosive Environments

doi:10.3390/met8040225

CORC > 金属研究所 > 中国科学院金属研究所

	Influence of Scandium Addition on Stress Corrosion Cracking Susceptibility of Al-Zn-Mg Alloy in Different Corrosive Environments
	Li, Zhaoming 1,2; Jiang, Haichang 1; Yan, Desheng 1; Rong, Lijian 1
刊名	METALS
	2018-04-01
卷号	8 期号:4 页码:12
关键词	Al-Zn-Mg alloy solution pH strain rate stress corrosion cracking susceptibility
ISSN号	2075-4701
DOI	10.3390/met8040225
通讯作者	Jiang, Haichang(hcjiang@imr.ac.cn) ; Rong, Lijian(ljrong@imr.ac.cn)
英文摘要	Stress corrosion cracking (SCC) susceptibilities of Al-Zn-Mg alloys without and with Scandium addition were evaluated in 3.5% NaCl solution at different pH and different strain rate, using slow strain rate test technique. The results indicate that Sc addition reduces grain size and width of precipitation free zones, and transforms grain boundary precipitates from continuous distribution into interrupted distribution by inhibiting recrystallization. In solution at pH 1, pH 3 and pH 7, Sc addition reduces the degree of localized corrosion of alloy surface and SCC susceptibility of Al-Zn-Mg alloy. However, in solution at pH 10 and pH 12, grain refinement significantly promotes the diffusion of hydrogen atoms into matrix, thus Sc addition increases SCC susceptibility of Al-Zn-Mg alloy. Under different strain rate conditions, Sc addition can all reduce SCC susceptibility of Al-Zn-Mg alloy in solution at pH 1, pH 3 and pH 7, and can all increase SCC susceptibility of Al-Zn-Mg alloy in solution at pH 10 and pH 12. As a result, Sc modified Al-Zn-Mg alloy in practical applications should be avoided in alkaline environments.
资助项目	State's Key Project of Research and Development[2016YFB1200600] ; Strategic Priority Program of the Chinese Academy of Sciences[XDB22000000]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	MDPI
WOS记录号	WOS:000434882800028
资助机构	State's Key Project of Research and Development ; Strategic Priority Program of the Chinese Academy of Sciences
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/128574]
专题	金属研究所_中国科学院金属研究所
通讯作者	Jiang, Haichang; Rong, Lijian
作者单位	1.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China 2.Univ Chinese Acad Sci, 19 Yuquan Rd, Beijing 100049, Peoples R China
推荐引用方式 GB/T 7714	Li, Zhaoming,Jiang, Haichang,Yan, Desheng,et al. Influence of Scandium Addition on Stress Corrosion Cracking Susceptibility of Al-Zn-Mg Alloy in Different Corrosive Environments[J]. METALS,2018,8(4):12.
APA	Li, Zhaoming,Jiang, Haichang,Yan, Desheng,&Rong, Lijian.(2018).Influence of Scandium Addition on Stress Corrosion Cracking Susceptibility of Al-Zn-Mg Alloy in Different Corrosive Environments.METALS,8(4),12.
MLA	Li, Zhaoming,et al."Influence of Scandium Addition on Stress Corrosion Cracking Susceptibility of Al-Zn-Mg Alloy in Different Corrosive Environments".METALS 8.4(2018):12.