In-situ hot pressing solid-liquid reaction synthesis of dense titanium silicon carbide bulk ceramics | |
Zhou, YC; Sun, ZM; Chen, SQ; Zhang, Y | |
刊名 | MATERIALS RESEARCH INNOVATIONS |
1998-11-01 | |
卷号 | 2期号:3页码:142-146 |
关键词 | Ti3SiC2, synthesis solid-liquid reaction in-situ formation |
ISSN号 | 1432-8917 |
通讯作者 | Zhou, YC() |
英文摘要 | An in-situ hot pressing/solid-liquid reaction process was developed for the synthesis of dense polycrystalline Ti3SiC2 ceramics using Ti, Si, and graphite powders as starting materials. The present work demonstrated that this process was one of the most effective and simple methods for the preparation of dense bulk Ti3SiC2 materials. Lattice constants of a=3.068 and c=17.645 are calculated for Ti3SiC2 made through this process. The synthesis temperature influenced the phase composition, microstructure and mechanical properties of Ti3SiC2 prepared at different temperatures. And bulk materials with flexural strength of 480 MPa and fracture toughness of 7.88 MPa.m(1/2) were obtained at 1600 degrees C. The high fracture toughness and strength are discussed based on microstructure analysis. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | SPRINGER VERLAG |
WOS记录号 | WOS:000077148100003 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/108110] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhou, YC |
作者单位 | Chinese Acad Sci, Met Res Inst, Ceram & Composite Dept, Shenyang 10015, Peoples R China |
推荐引用方式 GB/T 7714 | Zhou, YC,Sun, ZM,Chen, SQ,et al. In-situ hot pressing solid-liquid reaction synthesis of dense titanium silicon carbide bulk ceramics[J]. MATERIALS RESEARCH INNOVATIONS,1998,2(3):142-146. |
APA | Zhou, YC,Sun, ZM,Chen, SQ,&Zhang, Y.(1998).In-situ hot pressing solid-liquid reaction synthesis of dense titanium silicon carbide bulk ceramics.MATERIALS RESEARCH INNOVATIONS,2(3),142-146. |
MLA | Zhou, YC,et al."In-situ hot pressing solid-liquid reaction synthesis of dense titanium silicon carbide bulk ceramics".MATERIALS RESEARCH INNOVATIONS 2.3(1998):142-146. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论