INVESTIGATION OF POST-COLD ROLLING AGING PROCESSES ON SOLUTIONIZED 7050 ALUMINUM ALLOY | |
Wang Dong; Ma Zongyi | |
刊名 | ACTA METALLURGICA SINICA |
2010-05-11 | |
卷号 | 46期号:5页码:581-588 |
关键词 | 7050 aluminum alloy cold rolling aging process mechanical property microstructure |
ISSN号 | 0412-1961 |
DOI | 10.3724/SP.J.1037.2009.00723 |
通讯作者 | Ma Zongyi(zyma@imr.ac.cn) |
英文摘要 | 7050 aluminum alloy samples were subjected to 67% cold rolling (CR) deformation after solution treatment, and then were aged at 120 degrees C. The dislocations introduced by the CR, increased the strength of the samples. The strength of the sample aged at 120 degrees C for 4 h (CR4) increased by 12.6% compared to that of T6 sample. The strength of the 7050 samples decreased with increasing the aging time due to the coarsening of heterogeneously-nucleated precipitates. However, the strength of the sample aged at 120 degrees C for 32 h is still higher than that of the T6 sample. Furthermore, the size and particle interval of the grain boundary precipitates increased as the aging time increased. The CR4 sample was aged at 165 degrees C for different times. The strength of the samples decreased with increasing the aging time due to the annihilation of dislocations and the growth of the precipitates. The strength of the sample aged at 165 degrees C for 6 h is similar to that of T76 sample. In the CR4 sample aged at 135-180 degrees C for 1 h, the number of dislocations reduced and the size of precipitates increased with increasing the temperature, which results in a decrease in the strength of the samples. |
资助项目 | National Basic Research Program of China[2005CB623708] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SCIENCE CHINA PRESS |
WOS记录号 | WOS:000278475200010 |
资助机构 | National Basic Research Program of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/102073] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Ma Zongyi |
作者单位 | Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Wang Dong,Ma Zongyi. INVESTIGATION OF POST-COLD ROLLING AGING PROCESSES ON SOLUTIONIZED 7050 ALUMINUM ALLOY[J]. ACTA METALLURGICA SINICA,2010,46(5):581-588. |
APA | Wang Dong,&Ma Zongyi.(2010).INVESTIGATION OF POST-COLD ROLLING AGING PROCESSES ON SOLUTIONIZED 7050 ALUMINUM ALLOY.ACTA METALLURGICA SINICA,46(5),581-588. |
MLA | Wang Dong,et al."INVESTIGATION OF POST-COLD ROLLING AGING PROCESSES ON SOLUTIONIZED 7050 ALUMINUM ALLOY".ACTA METALLURGICA SINICA 46.5(2010):581-588. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论