Thermal Fatigue Behavior of Single-Crystal Superalloy | |
Liu Yuan1,2; Yu Jinjiang1; Xu Yan1; Sun Xiaofeng1 | |
刊名 | RARE METAL MATERIALS AND ENGINEERING
![]() |
2009 | |
卷号 | 38期号:1页码:59-63 |
关键词 | single-crystal superalloy thermal fatigue crack initiation and propagation |
ISSN号 | 1002-185X |
通讯作者 | Liu Yuan(yuanliu@imr.ac.cn) |
英文摘要 | The effects of cycle temperatures on the thermal fatigue crack growth of three kinds of superalloys were investigated. The experimental results show that the crack growth rate increases with the rise of cycle temperature. Optical Microscopy (OM) and Scanning electron microscopy (SEM) observations reveal that multiple small cracks primarily initiated at the notch tip in any temperature range. Subsequently, only one or two small cracks can continue to grow, and finally form the main cracks. The crack growth behavior varies distinctly for different alloys. In general, thermal fatigue cracks propagate along a preferential direction with the dendrite growth direction in single crystal superalloy, but along the interdendritic region for the Mar-M002 alloy. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000262955600014 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/96877] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Liu Yuan |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Liu Yuan,Yu Jinjiang,Xu Yan,et al. Thermal Fatigue Behavior of Single-Crystal Superalloy[J]. RARE METAL MATERIALS AND ENGINEERING,2009,38(1):59-63. |
APA | Liu Yuan,Yu Jinjiang,Xu Yan,&Sun Xiaofeng.(2009).Thermal Fatigue Behavior of Single-Crystal Superalloy.RARE METAL MATERIALS AND ENGINEERING,38(1),59-63. |
MLA | Liu Yuan,et al."Thermal Fatigue Behavior of Single-Crystal Superalloy".RARE METAL MATERIALS AND ENGINEERING 38.1(2009):59-63. |