Synthesis, Crystal Structure, and Physical Properties of Layered LnCrSe(2)O (Ln = Ce Nd) | |
Zhang, Xian; Xiao, Yi; Wang, Ruiqi; He, Jianqiao; Wang, Dong; Bu, Kejun; Mu, Gang; Huang, Fuqiang | |
刊名 | INORGANIC CHEMISTRY |
2019-07-15 | |
卷号 | 58期号:14页码:9482 |
ISSN号 | 0020-1669 |
DOI | 10.1021/acs.inorgchem.9b01364 |
文献子类 | Article |
英文摘要 | The layered oxyselenides with the formula LnCrSe2O (Ln = Ce Nd) were synthesized via molten salt methods. The isostructural compounds crystallize in the monoclinic space group of C2/m. The crystal structures feature 200[CrSe20]3 motifs stacked along the a axis, which are separated by Ln3 ions. The 2,0[CrSe20]3- layers are composed of [CrlSe6]9and [Cr2Se402]9- octahedra via corner and edge sharing. Powder X-ray diffraction results confirm the phase purities of the as-synthesized compounds. LnCrSe2O (Ln = Ce Nd) show typical antiferromagnetic ordering with TN = 125, 120, and 118 K, respectively. Heat capacity measurement for NdCrSe2O indicates that the Debye temperature is 278.4 K. Similar metal-to semiconductor phase transitions were observed for LnCrSe2O (Ln = Ce Nd) plates with transition temperatures of 115, 109, and 95 K, respectively. NdCrSe2O also possesses a magnetoresistance effect at low temperature (<25 K) with a significant positive magneto resistance,--, 16% at 2 K and 1 T. |
WOS研究方向 | Chemistry |
语种 | 英语 |
出版者 | AMER CHEMICAL SOC |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/26973] |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Zhang, Xian,Xiao, Yi,Wang, Ruiqi,et al. Synthesis, Crystal Structure, and Physical Properties of Layered LnCrSe(2)O (Ln = Ce Nd)[J]. INORGANIC CHEMISTRY,2019,58(14):9482. |
APA | Zhang, Xian.,Xiao, Yi.,Wang, Ruiqi.,He, Jianqiao.,Wang, Dong.,...&Huang, Fuqiang.(2019).Synthesis, Crystal Structure, and Physical Properties of Layered LnCrSe(2)O (Ln = Ce Nd).INORGANIC CHEMISTRY,58(14),9482. |
MLA | Zhang, Xian,et al."Synthesis, Crystal Structure, and Physical Properties of Layered LnCrSe(2)O (Ln = Ce Nd)".INORGANIC CHEMISTRY 58.14(2019):9482. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论