Mesoporous carbon supported MgO for CO2 capture and separation of CO2/N-2 | |
Burri, Harshitha1; Anjum, Rumana1; Gurram, Ramesh Babu2; Mitta, Harisekhar3; Mutyala, Suresh4,5; Jonnalagadda, Madhavi1 | |
刊名 | KOREAN JOURNAL OF CHEMICAL ENGINEERING |
2019-09-01 | |
卷号 | 36期号:9页码:1482-1488 |
关键词 | MgO Mesoporous Carbon CO2 and N-2 Adsorption Selectivity Heat of CO2 Adsorption |
ISSN号 | 0256-1115 |
DOI | 10.1007/s11814-019-0346-3 |
通讯作者 | Jonnalagadda, Madhavi(madhavi0521@gmail.com) |
英文摘要 | Mesoporous carbon derived from pongamia pinnata fruit hulls was used as support to incorporate magnesium oxide for the study of CO2 adsorption and separation of CO2/N-2. All synthesized adsorbents were characterized by PXRD, N-2 adsorption-desorption isotherms, Raman and SEM with EDX techniques. Characterization results revealed the existence of magnesium oxide on mesoporous carbon. CO2 adsorption on MgO incorporated mesoporous carbon was higher than bulk mesoporous carbon, due to the electrostatic interaction between magnesium oxide and CO2. High CO2 adsorption capacity 1.68 mmol/g was obtained for 10 wt% MgO incorporated mesoporous carbon at 298 K, 1 bar compared to remaining loadings, because of the high content of MgO. However, the N-2 adsorption capacity decreased with the increase of MgO content due to a decrease in surface area and no interaction of the N-2 molecule with the adsorbent. The selectivity of CO2/N-2 was higher on 10 wt% MgO incorporated mesoporous carbon and the value was 40. The heat of CO2 adsorption was 36KJ/mol at low coverage of CO2, and CO2 adsorption capacity was constant in each adsorption cycle over the same adsorbent. |
资助项目 | Science and Engineering Research Board, Department of Science and Technology, New Delhi, India[EMEQ-283/2014] |
WOS关键词 | ACTIVATED CARBON ; ADSORPTION PERFORMANCE ; POROUS CARBON ; DIOXIDE ; NITROGEN ; ADSORBENTS ; ISOTHERMS ; KINETICS ; METHANE |
WOS研究方向 | Chemistry ; Engineering |
语种 | 英语 |
出版者 | KOREAN INSTITUTE CHEMICAL ENGINEERS |
WOS记录号 | WOS:000483704500012 |
资助机构 | Science and Engineering Research Board, Department of Science and Technology, New Delhi, India ; Science and Engineering Research Board, Department of Science and Technology, New Delhi, India ; Science and Engineering Research Board, Department of Science and Technology, New Delhi, India ; Science and Engineering Research Board, Department of Science and Technology, New Delhi, India ; Science and Engineering Research Board, Department of Science and Technology, New Delhi, India ; Science and Engineering Research Board, Department of Science and Technology, New Delhi, India ; Science and Engineering Research Board, Department of Science and Technology, New Delhi, India ; Science and Engineering Research Board, Department of Science and Technology, New Delhi, India |
内容类型 | 期刊论文 |
源URL | [http://cas-ir.dicp.ac.cn/handle/321008/173306] |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
通讯作者 | Jonnalagadda, Madhavi |
作者单位 | 1.Govt Degree Coll Women, Dept Chem, Karimnagar, Telangana, India 2.Indian Inst Chem Technol, Catalysis Lab, Hyderabad 500007, Telangana, India 3.Chinese Acad Sci, State Key Lab Catalysis, Dalian Inst Chem Phys, Dalian 116023, Peoples R China 4.Shantou Univ, Dept Chem, Shantou 515063, Guangdong, Peoples R China 5.Shantou Univ, Key Lab Preparat & Applicat Ordered Struct Mat Gu, Shantou 515063, Guangdong, Peoples R China |
推荐引用方式 GB/T 7714 | Burri, Harshitha,Anjum, Rumana,Gurram, Ramesh Babu,et al. Mesoporous carbon supported MgO for CO2 capture and separation of CO2/N-2[J]. KOREAN JOURNAL OF CHEMICAL ENGINEERING,2019,36(9):1482-1488. |
APA | Burri, Harshitha,Anjum, Rumana,Gurram, Ramesh Babu,Mitta, Harisekhar,Mutyala, Suresh,&Jonnalagadda, Madhavi.(2019).Mesoporous carbon supported MgO for CO2 capture and separation of CO2/N-2.KOREAN JOURNAL OF CHEMICAL ENGINEERING,36(9),1482-1488. |
MLA | Burri, Harshitha,et al."Mesoporous carbon supported MgO for CO2 capture and separation of CO2/N-2".KOREAN JOURNAL OF CHEMICAL ENGINEERING 36.9(2019):1482-1488. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论