Crystallization design of MnO2 towards better supercapacitance | |
Zhang YJ ; Sun CT ; Lu P ; Li KY ; Song SY ; Xue DF | |
刊名 | crystengcomm |
2012 | |
卷号 | 14期号:18页码:5892-5897 |
关键词 | LI-ION BATTERIES HIGH-PERFORMANCE ELECTROCHEMICAL SUPERCAPACITORS HYDROTHERMAL SYNTHESIS CATHODE MATERIALS ENERGY-STORAGE CAPACITORS ELECTRODES NANOBELTS ROUTE |
ISSN号 | 1466-8033 |
通讯作者 | xue df |
中文摘要 | nanostructured manganese oxides with different crystallization behaviors were fabricated by a simple redox reaction between kmno4 and nano2 aqueous solution. mno2 nanostructures with sphere-, rod-, wire-, plate-and flower-like morphologies were crystallized, and the relationship between crystallization characteristics and their electrochemical performances were studied. the electrochemical energy storage behaviors of these samples were investigated by cyclic voltammetry and galvanostatic charge-discharge measurements processed using noncorrosive na2so4 as the electrolyte. a maximum specific capacitance 200 f g(-1) was obtained for poorly crystallized alpha-mno2 at a current density of 1 a g(-1). for different crystallographic mno2 phases, their specific capacitance values increase in the order: beta < gamma < delta < alpha, meanwhile, for any particular mno2 phase, their electrochemical energy storage performances decrease with increasing crystalline nature and particle size. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000307590700035 |
公开日期 | 2013-06-09 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/48437] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Zhang YJ,Sun CT,Lu P,et al. Crystallization design of MnO2 towards better supercapacitance[J]. crystengcomm,2012,14(18):5892-5897. |
APA | Zhang YJ,Sun CT,Lu P,Li KY,Song SY,&Xue DF.(2012).Crystallization design of MnO2 towards better supercapacitance.crystengcomm,14(18),5892-5897. |
MLA | Zhang YJ,et al."Crystallization design of MnO2 towards better supercapacitance".crystengcomm 14.18(2012):5892-5897. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论