Fabrication of novel thermal barrier coating on polymer composites via the combined sol-gel/sealing treatment process | |
Huang WZ ; Zou BL ; Zhao Y ; Meng XS ; Wang CJ ; Cao XQ ; Wang Z | |
刊名 | applied surface science |
2012 | |
卷号 | 258期号:22页码:9058-9066 |
关键词 | FUNCTIONALLY GRADED COATINGS SPRAYED OXIDE COATINGS MATRIX COMPOSITES ALUMINUM PHOSPHATE THIN-FILMS ZIRCONIA MICROSTRUCTURE OXIDATION ALLOY |
ISSN号 | 0169-4332 |
通讯作者 | cao xq |
中文摘要 | thermal barrier coating on the polyimide matrix composites was successfully fabricated at 400 degrees c via the combined sol-gel/sealing treatment process. in this approach, zirconia coating was firstly deposited onto substrate by sol-gel process, followed by penetration of aluminum phosphate into the final coating. sealing mechanisms of phosphate sealant were based on the adhesive binding of phosphates and the chemical bonding. after thermal cycling at 400 degrees c for 135 cycles, no apparent delaminations and spallations appeared in the zro2/phosphates dual coating, and the average bonding strength was 5.83 mpa. thermal oxidation of substrate coated with the zro2/phosphates dual coating could be retarded at about 900 degrees c. crown copyright (c) 2012 published by elsevier b. v. all rights reserved. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000306134900101 |
公开日期 | 2013-04-23 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/47981] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Huang WZ,Zou BL,Zhao Y,et al. Fabrication of novel thermal barrier coating on polymer composites via the combined sol-gel/sealing treatment process[J]. applied surface science,2012,258(22):9058-9066. |
APA | Huang WZ.,Zou BL.,Zhao Y.,Meng XS.,Wang CJ.,...&Wang Z.(2012).Fabrication of novel thermal barrier coating on polymer composites via the combined sol-gel/sealing treatment process.applied surface science,258(22),9058-9066. |
MLA | Huang WZ,et al."Fabrication of novel thermal barrier coating on polymer composites via the combined sol-gel/sealing treatment process".applied surface science 258.22(2012):9058-9066. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论