Improved oxidation resistance of Mo-12Si-8.5B composite at 1400 degrees C due to development of Zr-rich borosilicate scale | |
Wang, Juan; Li, Bin; Li, Rui; Wang, Tao; Chen, Xuan; Zhang, Guojun | |
2019 | |
卷号 | 45页码:3111-3117 |
关键词 | Composites ZrB2 addition Amorphous oxides Oxidation |
ISSN号 | 0272-8842 |
DOI | 10.1016/j.ceramint.2018.10.203 |
URL标识 | 查看原文 |
WOS记录号 | WOS:000456225900024 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/4970072 |
专题 | 西安理工大学 |
推荐引用方式 GB/T 7714 | Wang, Juan,Li, Bin,Li, Rui,et al. Improved oxidation resistance of Mo-12Si-8.5B composite at 1400 degrees C due to development of Zr-rich borosilicate scale[J],2019,45:3111-3117. |
APA | Wang, Juan,Li, Bin,Li, Rui,Wang, Tao,Chen, Xuan,&Zhang, Guojun.(2019).Improved oxidation resistance of Mo-12Si-8.5B composite at 1400 degrees C due to development of Zr-rich borosilicate scale.,45,3111-3117. |
MLA | Wang, Juan,et al."Improved oxidation resistance of Mo-12Si-8.5B composite at 1400 degrees C due to development of Zr-rich borosilicate scale".45(2019):3111-3117. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论