Fabrication, interfacial characteristics and strengthening mechanisms of ZrB2 microparticles reinforced Cu composites prepared by hot-pressed sintering | |
Wang, Chenchen[1,2]; Lin, Huaijun[1,2]; Zhang, Zhiguo[1,2]; Li, Wei[1,2] | |
2018 | |
卷号 | 748页码:546 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/4623962 |
专题 | 暨南大学 |
作者单位 | 1.[1]Jinan Univ, Inst Adv Wear & Corros Resistant & Funct Mat, Guangzhou 510632, Guangdong, Peoples R China 2.[2]Engn Res Ctr Wear Resistant Mat & Special Funct M, Guangzhou 510632, Guangdong, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Chenchen[1,2],Lin, Huaijun[1,2],Zhang, Zhiguo[1,2],et al. Fabrication, interfacial characteristics and strengthening mechanisms of ZrB2 microparticles reinforced Cu composites prepared by hot-pressed sintering[J],2018,748:546. |
APA | Wang, Chenchen[1,2],Lin, Huaijun[1,2],Zhang, Zhiguo[1,2],&Li, Wei[1,2].(2018).Fabrication, interfacial characteristics and strengthening mechanisms of ZrB2 microparticles reinforced Cu composites prepared by hot-pressed sintering.,748,546. |
MLA | Wang, Chenchen[1,2],et al."Fabrication, interfacial characteristics and strengthening mechanisms of ZrB2 microparticles reinforced Cu composites prepared by hot-pressed sintering".748(2018):546. |