THE INFLUENCE OF PRESTRAIN AND AGING ON NEAR-THRESHOLD FATIGUE-CRACK PROPAGATION IN AS-ROLLED AND HEAT-TREATED DUAL-PHASE STEELS | |
Y. S. Zheng ; Z. G. Wang ; S. H. Ai | |
刊名 | Steel Research
![]() |
1991 | |
卷号 | 62期号:5页码:223-227 |
关键词 | growth strength |
ISSN号 | 0177-4832 |
中文摘要 | The influence of prestrain and ageing on near-threshold fatigue-crack propagation (FCP) in as-rolled and heat-treated dualphase steels (DPS) was investigated over a wide range of 10(-10) to 10(-7) mm/cycle in laboratory air under a load ratio of R = 0. It was found that the fatigue-crack propagation threshold value increases with increasing grain size and decreasing yield stress, and that a combination of 10% prestraining with 175-degrees-C/30 min ageing showed almost no effect on the threshold level of as-rolled dual-phase steel, but decreased that of heat-treated dual-phase steels more than 37%. This different behaviour was suggested to result from the remarkable differences in grain size and volume fraction of martensite (Vm) in these two kinds of dual-phase steels. An estimation of the plastic zone size of fatigue-crack tip supported this suggestion. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/39528] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Y. S. Zheng,Z. G. Wang,S. H. Ai. THE INFLUENCE OF PRESTRAIN AND AGING ON NEAR-THRESHOLD FATIGUE-CRACK PROPAGATION IN AS-ROLLED AND HEAT-TREATED DUAL-PHASE STEELS[J]. Steel Research,1991,62(5):223-227. |
APA | Y. S. Zheng,Z. G. Wang,&S. H. Ai.(1991).THE INFLUENCE OF PRESTRAIN AND AGING ON NEAR-THRESHOLD FATIGUE-CRACK PROPAGATION IN AS-ROLLED AND HEAT-TREATED DUAL-PHASE STEELS.Steel Research,62(5),223-227. |
MLA | Y. S. Zheng,et al."THE INFLUENCE OF PRESTRAIN AND AGING ON NEAR-THRESHOLD FATIGUE-CRACK PROPAGATION IN AS-ROLLED AND HEAT-TREATED DUAL-PHASE STEELS".Steel Research 62.5(1991):223-227. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论