INTRINSIC MAGNETIC-PROPERTIES OF R2FE17CYNXCOMPOUNDS - (R=Y, SM, ER, AND TM)

CORC > 金属研究所 > 中国科学院金属研究所

	INTRINSIC MAGNETIC-PROPERTIES OF R2FE17CYNXCOMPOUNDS - (R=Y, SM, ER, AND TM)
	X. C. Kou ; R. Grossinger ; M. Katter ; J. Wecker ; L. Schultz ; T. H. Jacobs ; K. H. J. Buschow
刊名	Journal of Applied Physics
	1991
卷号	70 期号:4 页码:2272-2282
关键词	magnetocrystalline anisotropy carbides alloys
ISSN号	0021-8979
中文摘要	Samples of R2Fe17C(y)N(x) (R = Y, Sm, Er, Tm) were prepared by arc melting appropriate amount of R, Fe, and C, vacuum annealing at 1373 K and finally annealing at 740 K in nitrogen for 10 h. The magnetic properties of these compounds were investigated by means of ac initial susceptibility, magnetization measurements, and x-ray diffraction. The thermal stability of the nitride phase was studied by differential scanning calorimetry. It was found that, when heated above 600 K, R2Fe17C(y)N(x) irreversibly decomposes N which is irrespective of the carbon concentration and rare-earth element. The Curie temperatures of R2Fe17C(y)N(x) are independent of the carbon concentration and are approximately 400 K higher than those of the corresponding pure R2Fe17 compounds. However, the Curie temperatures cannot be correlated to the composition x of the initial R2Fe17C(y)N(x) compounds at room temperature because some N was lost during the heating to T(c). In the Er and Tm compounds spin reorientation transitions were found, marking the change of the easy magnetization direction from the c axis to the basal plane with increasing temperature. The Tm compounds show an additional magnetic transition at low temperatures (below 40 K). A coexistence of the hexagonal and the rhombohedral structural modifications was found in Er2Fe17C(y)N(x) when y < 1.5, characterized by two different spin reorientation temperatures. The anisotropy fields of Sm2Fe17C(y)N(x) are higher than that of Sm2Fe17N(x). Indications of a magnetic phase transition were found also in Sm2Fe17C0.7N(x) and Sm2Fe17C0.9N(x).
原文出处	://WOS:A1991GC09800056
公开日期	2012-04-14
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/39407]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	X. C. Kou,R. Grossinger,M. Katter,et al. INTRINSIC MAGNETIC-PROPERTIES OF R2FE17CYNXCOMPOUNDS - (R=Y, SM, ER, AND TM)[J]. Journal of Applied Physics,1991,70(4):2272-2282.
APA	X. C. Kou.,R. Grossinger.,M. Katter.,J. Wecker.,L. Schultz.,...&K. H. J. Buschow.(1991).INTRINSIC MAGNETIC-PROPERTIES OF R2FE17CYNXCOMPOUNDS - (R=Y, SM, ER, AND TM).Journal of Applied Physics,70(4),2272-2282.
MLA	X. C. Kou,et al."INTRINSIC MAGNETIC-PROPERTIES OF R2FE17CYNXCOMPOUNDS - (R=Y, SM, ER, AND TM)".Journal of Applied Physics 70.4(1991):2272-2282.