Effect of Pr content in Ml on the electrochemical properties of Ml(Ni-Co-Mn-Al)(5) alloys | |
Z. H. Chen ; M. Q. Lu ; Y. L. Wang ; Z. Q. Hu | |
刊名 | Journal of Alloys and Compounds
![]() |
1995 | |
卷号 | 231期号:1-2页码:550-552 |
关键词 | Pr Ml electrochemical properties Ml-Ni alloys hydrogen batteries electrodes hydrides storage lani5 |
ISSN号 | 0925-8388 |
中文摘要 | The electrochemical properties of MINi(3.5)Co(0.8)Mn(0.4)Al(0.3) alloys with various Pr contents in MI were studied in this work, It was found that the Pr content in MI obviously affected the electrochemical properties of MI(Ni-Co-Mn-Al)(5) alloys. The electrochemical properties were greatly improved if the electrode alloy contained about 20 at.% Pr in MI. The electrode made from this alloy has a higher capacity, better discharge rate characteristics and longer cycle life than that from alloy with less than 10 at.% Pr in MI, as in common misch metal. The AA size cells in which electrode alloy contains about 17 at% Pr in MI are also studied. It was found that these cells have a very long cycle life (1400 cycles) with reasonable capacity (1250 mA h) and rate capability (1100 mAh) when discharged at 5 C). In particular, they have a very superior low temperature capability. For example, their capacity was higher than 1050 mA h when discharged at 1C and -18 degrees C. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/38539] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Z. H. Chen,M. Q. Lu,Y. L. Wang,et al. Effect of Pr content in Ml on the electrochemical properties of Ml(Ni-Co-Mn-Al)(5) alloys[J]. Journal of Alloys and Compounds,1995,231(1-2):550-552. |
APA | Z. H. Chen,M. Q. Lu,Y. L. Wang,&Z. Q. Hu.(1995).Effect of Pr content in Ml on the electrochemical properties of Ml(Ni-Co-Mn-Al)(5) alloys.Journal of Alloys and Compounds,231(1-2),550-552. |
MLA | Z. H. Chen,et al."Effect of Pr content in Ml on the electrochemical properties of Ml(Ni-Co-Mn-Al)(5) alloys".Journal of Alloys and Compounds 231.1-2(1995):550-552. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论