The valence and transport property studies for the solid solution Ce1-xEuxO2-delta synthesized by high-temperature and high-pressure | |
Y. L. Che ; L. P. Li ; G. S. Li ; Z. Lu ; X. M. Lin ; J. Xiang ; W. H. Su | |
刊名 | Chemical Journal of Chinese Universities-Chinese |
2001 | |
卷号 | 22期号:3页码:368-370 |
关键词 | high-temperature and high-pressure valence state transport property hydrothermal synthesis (ceo2)(1-x)(bio1.5)(x) conduction xps |
ISSN号 | 0251-0790 |
中文摘要 | The solid solutions Ce1-xEuxO2-delta (x = 0.10-0.50) were synthesized by high-temperature and high-pressure, The XRD measurement showed that the solid solution was crystallized in cubic fluorite-type structure and the lattice parameter increased with the content of Eu increasing up to x = 0.4. The solution limit was ca. 0.4 under the condition of 3.6 GPa, 840-1020 degreesC. The XPS data showed that the Eu ions are Eu3+ and trace of Ce4+ ions were reduced to Ce3+ ions during synthesis of high-temperature and high-pressure. The ionic conduction for Ce0.8Eu0.2O2-delta was measured by impedance spectroscopy and it was found that the activation energy was 1.07 eV and the conductivity was 3.43 x 10(-5) S.cm(-1) at 550 degreesC. |
原文出处 | |
公开日期 | 2012-04-14 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/36604] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Y. L. Che,L. P. Li,G. S. Li,et al. The valence and transport property studies for the solid solution Ce1-xEuxO2-delta synthesized by high-temperature and high-pressure[J]. Chemical Journal of Chinese Universities-Chinese,2001,22(3):368-370. |
APA | Y. L. Che.,L. P. Li.,G. S. Li.,Z. Lu.,X. M. Lin.,...&W. H. Su.(2001).The valence and transport property studies for the solid solution Ce1-xEuxO2-delta synthesized by high-temperature and high-pressure.Chemical Journal of Chinese Universities-Chinese,22(3),368-370. |
MLA | Y. L. Che,et al."The valence and transport property studies for the solid solution Ce1-xEuxO2-delta synthesized by high-temperature and high-pressure".Chemical Journal of Chinese Universities-Chinese 22.3(2001):368-370. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论