Effect of Dy2O3 on the hot corrosion of Ni-based superalloy K3 beneath Na2SO4-V2O5 film at 1073K in air by electrochemical impedance spectroscopy | |
C. Song ; C. L. Zeng | |
刊名 | High Temperature Materials and Processes |
2007 | |
卷号 | 26期号:5-6页码:377-389 |
关键词 | nickel-based alloy K3 Na2SO4-V2O5 Dy2O3 MgO hot corrosion electrochemical impedance spectroscopy high-temperature corrosion oil ash corrosion fuel impurities steam boilers sodium oxide solubilities inhibitor mechanism zirconia |
ISSN号 | 0334-6455 |
中文摘要 | This paper reports comparative investigations of the effects of Dy2O3 and MgO additives on the hot corrosion of nickel-based alloy K3 beneath Na2SO4-V2O5 film at 1073K in air by using electrochemical impedance spectroscopy. It was shown that the Dy2O3 additive could react with V2O5 to form a refractory compound DyVO4, and reduced dramatically the corrosion of the alloy due to the formation of a porous, friable deposit and of a protective Cr2O3-rich layer. Correspondingly, the electrochemical impedance spectra were composed of two capacitive loops. In contrast, the electrochemical impedance spectra for the corrosion in both Na2SO4-V2O5 and Na2SO4-MgO environments exhibited the typical features of a diffusion-controlled reaction. The MgO additive could decrease the corrosiveness of Na2SO4-V2O5 by the formation of magnesium vanadates and promoting the formation of a protective Cr-enriched scale, but with less effectiveness than the Dy2O3 additive. |
原文出处 | |
公开日期 | 2012-04-13 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/33812] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | C. Song,C. L. Zeng. Effect of Dy2O3 on the hot corrosion of Ni-based superalloy K3 beneath Na2SO4-V2O5 film at 1073K in air by electrochemical impedance spectroscopy[J]. High Temperature Materials and Processes,2007,26(5-6):377-389. |
APA | C. Song,&C. L. Zeng.(2007).Effect of Dy2O3 on the hot corrosion of Ni-based superalloy K3 beneath Na2SO4-V2O5 film at 1073K in air by electrochemical impedance spectroscopy.High Temperature Materials and Processes,26(5-6),377-389. |
MLA | C. Song,et al."Effect of Dy2O3 on the hot corrosion of Ni-based superalloy K3 beneath Na2SO4-V2O5 film at 1073K in air by electrochemical impedance spectroscopy".High Temperature Materials and Processes 26.5-6(2007):377-389. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论